Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | TD | ISO294-4 | 0.40 | % |
Modeling Shrinkage | MD | ISO294-4 | 0.10 | % |
Moisture Absorption | Equilibrium,23°C,50%RH | ISO62 | 0.030 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | Break | ISO527-2/1A/5 | 150 | Mpa |
Tensile Strain | Break | ISO527-2/1A/5 | 1.6 | % |
Tensile Modulus | | ISO527-2/1A/1 | 15000 | Mpa |
Flexural Modulus | 23°C | ISO178 | 13500 | Mpa |
Compressive Modulus | | ISO604 | 14000 | Mpa |
Flexural Stress | 23°C | ISO178 | 220 | Mpa |
CompressiveStress | 1%Strain | ISO604 | 93.0 | Mpa |
Flexural Strain (Break) | | ISO178 | 2.2 | % |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Vicat Softening Temperature | | ISO306/B50 | 195 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 276 | °C |
Deflection Temperature Under Load? | 8.0MPa,Unannealed | ISO75-2/C | 216 | °C |
Linear thermal expansion coefficient | MD | ISO11359-2 | 7E-06 | cm/cm/°C |
Linear thermal expansion coefficient | TD | ISO11359-2 | 2E-05 | cm/cm/°C |
Melting Temperature | | ISO11357-3 | 335 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Relative Permittivity | 100Hz | IEC60250 | 4.00 | |
Relative Permittivity | 1MHz | IEC60250 | 3.30 | |
Relative Permittivity | 2.05GHz | 内部方法 | 4.23 | |
Comparative Tracking Index | | IEC60112 | 175 | V |
Dissipation Factor? | 100Hz | IEC60250 | 0.010 | |
Dissipation Factor? | 1MHz | IEC60250 | 0.025 | |
Dissipation Factor? | 2.05GHz | 内部方法 | 6E-03 | |
Surface Resistivity | | IEC60093 | 1E+14 | ohms |
Arc Resistance | | 内部方法 | 140 | sec |
Volume Resistivity | | IEC60093 | 1E+15 | ohms·cm |
Dielectric Strength | | IEC60243-1 | 32 | KV/mm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Notched Izod impact strength | 23°C | ISO180/1U | 31 | kJ/m² |
Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 43 | kJ/m² |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | M-Scale | ISO2039-2 | 71 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | | UL94 | V-0 | |
Oxygen Index | | ISO4589-2 | 45 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.