LCP SUMIKASUPER® E6007LHF-MR-Z SUMITOMO JAPAN

105

Unit Price:
$4961 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
152MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Low warpage Good forming performance Glass fiber reinforced enhance
Application Areas:Automotive sector
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	Across Flow	内部方法	0.60	%
Modeling Shrinkage	Modeling Shrinkage	流量	内部方法	0.20	%
Moisture Absorption	Saturation	ASTM D570	0.020	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Elongation	Break	ASTM D638	5.1	%
Flexural Modulus	23°C	ASTM D790	11800	Mpa
Flexural Strength	23°C	ASTM D790	158	Mpa
Tensile Strength		ASTM D638	157	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	1.8 MPa, Unannealed	ASTM D648	269	°C
Linear thermal expansion coefficient	Flow : 150°C	内部方法	2.0E-6	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	Across Flow : 150°C	内部方法	8.5E-5	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Comparative Tracking Index		IEC 60112	175	V
Dielectric Constant	1 MHz	ASTM D150	3.80
Dielectric Constant	Dielectric Constant	1.00 GHz	ASTM D150	3.50
Arc Resistance		ASTM D495	124	sec
Volume Resistivity		ASTM D257	1.0E+15	ohms·cm
Dissipation Factor?	1 MHz	ASTM D150	0.026
Dissipation Factor?	Dissipation Factor?	1.00 GHz	ASTM D150	4.0E-3

Injection	Test Result	Unit
Drying Temperature	130	°C
Processing (Melt) Temp	350	°C
Mold Temperature	40 到 160	°C
Holding Pressure	20.0 到 40.0	Mpa
Drying Time	4.0 到 24	hr
Rear Temperature	280 到 320	°C
Middle Temperature	320 到 340	°C
Front Temperature	340 到 360	°C
Nozzle Temperature	340 到 360	°C
Back Pressure	1.00 到 5.00	Mpa
Screw Speed	50 到 100	rpm
Injection Pressure	80.0 到 160	Mpa
Injection Rate	中等偏快

Impact Properties	Test Condition	Test Method	Test Result	Unit
Unnotched Izod Impact Strength	6.40 mm	ASTM D256	250	J/m

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	R-Scale	ASTM D785	106

Flammability	Test Condition	Test Method	Test Result	Unit
Oxygen Index		ISO 527-1,-2(JIS K7161,7162)	40	%
Flame Rating	0.30 mm, ALL	UL 94	V-0
Soldering Resistance		内部方法	300	°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.