LCP LAPEROS® E130i-BK205P JAPAN POLYPLASTIC
189
- Unit Price:
- $8351 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 100MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:heat-resisting Flame retardant enhance
- Application Areas:Household appliances Household appliances
- Color:--
- Grade:Injection grade
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD | ISO294-4 | 0.40 | % |
| MD | ISO294-4 | 0.10 | % | |
| Water absorption rate | Equilibrium,23°C,50%RH | ISO62 | 0.030 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress | Break | ISO527-2/1A/5 | 150 | Mpa |
| Tensile strain | Break | ISO527-2/1A/5 | 1.6 | % |
| Tensile modulus | ISO527-2/1A/1 | 15000 | Mpa | |
| Bending modulus | 23°C | ISO178 | 13500 | Mpa |
| Compressive modulus | ISO604 | 14000 | Mpa | |
| Bending stress | 23°C | ISO178 | 220 | Mpa |
| CompressiveStress | 1%Strain | ISO604 | 93.0 | Mpa |
| Fracture bending strain | ISO178 | 2.2 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat softening temperature | ISO306/B50 | 195 | °C | |
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 276 | °C |
| 8.0MPa,Unannealed | ISO75-2/C | 216 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 7E-06 | cm/cm/°C |
| TD | ISO11359-2 | 2E-05 | cm/cm/°C | |
| Melting temperature 2 | ISO11357-3 | 335 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Relative permittivity | 100Hz | IEC60250 | 4.00 | |
| 1MHz | IEC60250 | 3.30 | ||
| 2.05GHz | 内部方法 | 4.23 | ||
| Leakage Trace Index | IEC60112 | 175 | V | |
| Dissipation factor | 100Hz | IEC60250 | 0.010 | |
| 1MHz | IEC60250 | 0.025 | ||
| 2.05GHz | 内部方法 | 6E-03 | ||
| Surface resistivity | IEC60093 | 1E+14 | ohms | |
| Arc resistance | 内部方法 | 140 | sec | |
| Volume resistivity | IEC60093 | 1E+15 | ohms·cm | |
| Dielectric strength | IEC60243-1 | 32 | KV/mm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Unscented Izod impact strength | 23°C | ISO180/1U | 31 | kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 43 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | M-Scale | ISO2039-2 | 71 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | UL94 | V-0 | ||
| Extreme Oxygen Index | ISO4589-2 | 45 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.