LCP LAPEROS® E130i-BK210P JAPAN POLYPLASTIC
186
- Unit Price:
- $8812 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 246MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:heat-resisting Flame retardant enhance
- Application Areas:Household appliances Household appliances
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | TD | ISO294-4 | 0.40 | % |
| MD | ISO294-4 | 0.10 | % | |
| Moisture Absorption | Equilibrium,23°C,50%RH | ISO62 | 0.030 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Stress | Break | ISO527-2/1A/5 | 150 | Mpa |
| Tensile Strain | Break | ISO527-2/1A/5 | 1.6 | % |
| Tensile Modulus | ISO527-2/1A/1 | 15000 | Mpa | |
| Flexural Modulus | 23°C | ISO178 | 13500 | Mpa |
| Compressive Modulus | ISO604 | 14000 | Mpa | |
| Flexural Stress | 23°C | ISO178 | 220 | Mpa |
| CompressiveStress | 1%Strain | ISO604 | 93.0 | Mpa |
| Flexural Strain (Break) | ISO178 | 2.2 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat Softening Temperature | ISO306/B50 | 195 | °C | |
| Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 276 | °C |
| 8.0MPa,Unannealed | ISO75-2/C | 216 | °C | |
| Linear thermal expansion coefficient | MD | ISO11359-2 | 7E-06 | cm/cm/°C |
| TD | ISO11359-2 | 2E-05 | cm/cm/°C | |
| Melting Temperature | ISO11357-3 | 335 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Relative Permittivity | 100Hz | IEC60250 | 4.00 | |
| 1MHz | IEC60250 | 3.30 | ||
| 2.05GHz | 内部方法 | 4.23 | ||
| Comparative Tracking Index | IEC60112 | 175 | V | |
| Dissipation Factor? | 100Hz | IEC60250 | 0.010 | |
| 1MHz | IEC60250 | 0.025 | ||
| 2.05GHz | 内部方法 | 6E-03 | ||
| Surface Resistivity | IEC60093 | 1E+14 | ohms | |
| Arc Resistance | 内部方法 | 140 | sec | |
| Volume Resistivity | IEC60093 | 1E+15 | ohms·cm | |
| Dielectric Strength | IEC60243-1 | 32 | KV/mm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Notched Izod impact strength | 23°C | ISO180/1U | 31 | kJ/m² |
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 43 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell Hardness | M-Scale | ISO2039-2 | 71 |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | UL94 | V-0 | ||
| Oxygen Index | ISO4589-2 | 45 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.