LCP LAPEROS® E130i VF2201 JAPAN POLYPLASTIC
221
- Unit Price:
- $8369 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 105MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:heat-resisting Flame retardant enhance
- Application Areas:Household appliances Household appliances
- Color:--
- Grade:Injection grade
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD | ISO294-4 | 0.40 | % |
| MD | ISO294-4 | 0.10 | % | |
| Water absorption rate | Equilibrium,23°C,50%RH | ISO62 | 0.030 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO527-2/1A/1 | 15000 | Mpa | |
| Tensile stress | Break | ISO527-2/1A/5 | 150 | Mpa |
| Tensile strain | Break | ISO527-2/1A/5 | 1.6 | % |
| Bending modulus | 23°C | ISO178 | 13500 | Mpa |
| Bending stress | 23°C | ISO178 | 220 | Mpa |
| Compressive modulus | ISO604 | 14000 | Mpa | |
| CompressiveStress | 1%Strain | ISO604 | 93.0 | Mpa |
| Fracture bending strain | ISO178 | 2.2 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 276 | °C |
| 8.0MPa,Unannealed | ISO75-2/C | 216 | °C | |
| Vicat softening temperature | ISO306/B50 | 195 | °C | |
| Melting temperature 2 | ISO11357-3 | 335 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 7E-06 | cm/cm/°C |
| TD | ISO11359-2 | 2E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | 1E+14 | ohms | |
| Volume resistivity | IEC60093 | 1E+15 | ohms·cm | |
| Dielectric strength | IEC60243-1 | 32 | KV/mm | |
| Relative permittivity | 100Hz | IEC60250 | 4.00 | |
| 1MHz | IEC60250 | 3.30 | ||
| 2.05GHz | 内部方法 | 4.23 | ||
| Dissipation factor | 100Hz | IEC60250 | 0.010 | |
| 1MHz | IEC60250 | 0.025 | ||
| 2.05GHz | 内部方法 | 6E-03 | ||
| Arc resistance | 内部方法 | 140 | sec | |
| Leakage Trace Index | IEC60112 | 175 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 43 | kJ/m² |
| Unscented Izod impact strength | 23°C | ISO180/1U | 31 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | M-Scale | ISO2039-2 | 71 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | UL94 | V-0 | ||
| Extreme Oxygen Index | ISO4589-2 | 45 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.