Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melt Volume flow Rate | 230°C/3.8kg | ASTMD1505 | 7.00 | cm3/10min |
Modeling Shrinkage | | ISO294-4 | 0.50到0.70 | % |
Moisture Absorption | 23°C,24hr | ASTMD570,ISO62 | 0.15 | % |
-- | | ASTMD792,ISO1183/B | 1.13 | g/cm³ |
-- | | ISO11831 | 1130 | kg/m3 |
230°C/3.8kg | | ASTMD1238 | 3.7 | g/10min |
260°C/5.0kg | | ISO1133,ASTMD1238 | 18 | g/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
4.00mm,注塑 | | ISO527-2 | 2330 | Mpa |
Flexural Stress | | ISO178 | 90.0 | Mpa |
--9 | | ASTMD790 | 2450 | Mpa |
--10 | | ISO178 | 2400 | Mpa |
Tensile Elongation | Break | ISO527-28 | >50 | % |
Break | | ASTMD638 | 55.0 | Mpa |
yield | | ISO527-2/50 | 57.0 | Mpa |
yield | | ISO527-25 | 54.0 | Mpa |
yield | | ISO527-2/50 | 4.5 | % |
yield | | ISO527-27 | 4.4 | % |
fracture | | ASTMD638 | 160 | % |
fracture | | ISO527-2/50 | 90 | % |
fracture | | ISO527-2/50 | 47.0 | Mpa |
Yield | | ASTMD638 | 58.0 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
-- | | ISO306/A120 | 142 | °C |
-- | | ISO306/B50 | 129 | °C |
0.45MPa, Unannealed | | ISO75-2/B | 130 | °C |
1.8MPa, Unannealed | | ASTMD648 | 109 | °C |
1.8MPa, Unannealed | | ISO75-2/A | 106 | °C |
Coefficient of Linear Thermal Expansion (Flow) | | ISO11359-222 | 6.9E-05 | cm/cm/°C |
0.45MPa | | ISO75-219 | 126 | °C |
1.8MPa | | ISO75-220 | 105 | °C |
50°C/h,B50N | | ISO30621 | 124 | °C |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 62.0 | J |
Instrumented Dart Impact | 23°C,PeakEnergy | ASTMD3763 | 55.0 | J |
-30°C | | ISO180/A | 47 | kJ/m² |
-30°C | | 16 | 无断裂 | |
-30°C | | 13 | 14.0 | kJ/m² |
-30°C | | ASTMD256 | 590 | J/m |
23°C | | 14 | 40.0 | kJ/m² |
23°C | | ISO180/A | 63 | kJ/m² |
23°C | | 17 | 无断裂 | |
23°C | | ASTMD256 | 750 | J/m |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Burning Rate | | FMVSS302 | <100 | mm/min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.