Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | TD:260°C,2.00mm | ISO294-4 | 0.55到0.75 | % |
Modeling Shrinkage | MD:260°C,2.00mm | ISO294-4 | 0.55到0.75 | % |
Moisture Absorption | Saturation,23°C | ISO62 | 0.50 | % |
Moisture Absorption | Equilibrium,23°C,50%RH | ISO62 | 0.20 | % |
Melt Volume flow Rate | 260°C/5.0kg | ISO1133 | 26.0 | cm3/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | Yield,23°C | ISO527-2/50 | 61.0 | Mpa |
Tensile Stress | Break,23°C | ISO527-2/50 | 56.0 | Mpa |
Tensile Strain | Yield,23°C | ISO527-2/50 | 5.1 | % |
Tensile Strain | Break,23°C | ISO527-2/50 | >50 | % |
Tensile Modulus | 23°C | ISO527-2/1 | 2400 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 130 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 112 | °C |
Linear thermal expansion coefficient | MD:23to55°C | ISO11359-2 | 7E-05 | cm/cm/°C |
Linear thermal expansion coefficient | TD:23to55°C | ISO11359-2 | 7E-05 | cm/cm/°C |
Vicat Softening Temperature | -- | ISO306/B50 | 134 | °C |
Vicat Softening Temperature | -- | ISO306/B120 | 135 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Relative Permittivity | 23°C,100Hz | IEC60250 | 3.10 | |
Relative Permittivity | 23°C,1MHz | IEC60250 | 3.00 | |
Dielectric Strength | 23°C,1.00mm | IEC60243-1 | 35 | KV/mm |
Surface Resistivity | | IEC60093 | 1E+16 | ohms |
Volume Resistivity | 23°C | IEC60093 | 1E+16 | ohms·cm |
Dissipation Factor? | 23°C,100Hz | IEC60250 | 2.5E-03 | |
Dissipation Factor? | 23°C,1MHz | IEC60250 | 0.010 | |
Fill Analysis | Test Condition | Test Method | Test Result | Unit |
---|
Melt Viscosity | 260°C | ISO11443-A | 225 | Pa·s |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Multi-Axial Instrumented Impact Energy | -30°C | ISO6603-2 | 57.0 | J |
Multi-Axial Instrumented Impact Energy | 23°C | ISO6603-2 | 51.0 | J |
Notched Izod impact strength | 23°C | ISO180 | 无断裂 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.