Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Mass-Flow Rate | 240°C/5.0kg | ASTMD1238 | 7.0 | g/10min |
| Melt Mass-Flow Rate | 240°C/5.0kg | ISO1133 | 7.0 | g/10min |
| Density / Specific Gravity | | ASTMD792 | 1.15 | g/cm³ |
| Density / Specific Gravity | 23°C | ISO1183 | 1.15 | g/cm³ |
| Modeling Shrinkage | MD：3.20mm | ASTMD955 | 0.40to0.60 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Stress | Yield,23°C | ISO527-2 | 54.0 | Mpa |
| Flexural Stress | 23°C | ISO178 | 89.0 | Mpa |
| Tensile Strength | 23°C | ASTMD638 | 53.9 | Mpa |
| Flexural Modulus | 23°C | ASTMD790 | 2450 | Mpa |
| Flexural Modulus | 23°C | ISO178 | 2450 | Mpa |
| Flexural Strength | 23°C | ASTMD790 | 89.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 1.8MPa,Unannealed,6.35mm | ASTMD648 | 106 | °C |
| Deflection Temperature Under Load? | 1.8MPa,Unannealed,6.35mm | ISO75-2/A | 106 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Notched Izod Impact Strength | 23°C,3.18mm | ISO180 | 590 | J/m |
| Notched Izod Impact Strength | 23°C,3.18mm | ASTMD256 | 590 | J/m |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | R-Sale,23°C | ASTMD785 | 112 | |
| Rockwell Hardness | R-Sale,23°C | ISO2039-2 | 112 | |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.5mm,AllColors | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.