PC/ABS CYCOLOY™ CX7240-701 SABIC INNOVATIVE NANSHA
45
- Unit Price:
- $5930 USD/MT
- Packaging Specification:
- 25KG/PKG
- Supply Quantity:
- 165MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Modeling Shrinkage | MD:3.20mm | 内部方法 | 0.40to0.60 | % |
Moisture Absorption | Saturation,23°C | ISO62 | 0.20 | % |
Equilibrium,23°C,50%RH | ISO62 | 0.10 | % | |
Melt Mass-Flow Rate | 260°C/2.16kg | ASTMD1238 | 18 | g/10min |
Melt Volume flow Rate | 260°C/2.16kg | ISO1133 | 15.0 | cm3/10min |
Density / Specific Gravity | ASTMD792 | 1.19 | g/cm³ | |
ISO1183 | 1.20 | g/cm³ |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Tensile Elongation | Break | ASTMD638 | 100 | % |
Flexural Modulus | ISO178 | 2500 | Mpa | |
Flexural Strength | ISO178 | 96.0 | Mpa | |
Tensile Modulus | ISO527-2/1 | 2600 | Mpa | |
Tensile Elongation | Yield | ASTMD638 | 4.1 | % |
Tensile Modulus | ASTMD638 | 2600 | Mpa | |
Tensile Strength | Break | ASTMD638 | 58.0 | Mpa |
Yield | ASTMD638 | 65.0 | Mpa | |
Flexural Modulus | 50.0mmSpan | ASTMD790 | 2500 | Mpa |
Flexural Strength | Yield,50.0mmSpan | ASTMD790 | 104 | Mpa |
Tensile Stress | Yield | ISO527-2/50 | 65.0 | Mpa |
Break | ISO527-2/50 | 50.0 | Mpa | |
Tensile Strain | Break | ISO527-2/50 | 90 | % |
Yield | ISO527-2/50 | 4.0 | % |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
RTIElec | UL746 | 90.0 | °C | |
Evolution Calendar intelligent importer | UL746 | 90.0 | °C | |
RTIStr | UL746 | 90.0 | °C | |
Linear thermal expansion coefficient | MD:-40to40°C | ASTME831 | 7.5E-05 | cm/cm/°C |
MD:-40to40°C | ISO11359-2 | 7.5E-05 | cm/cm/°C | |
TD:-40to40°C | ASTME831 | 7.5E-05 | cm/cm/°C | |
TD:-40to40°C | ISO11359-2 | 7.5E-05 | cm/cm/°C | |
Deflection Temperature Under Load? | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 100 | °C |
1.8MPa,Unannealed,3.20mm | ASTMD648 | 89.0 | °C | |
1.8MPa,Unannealed,6.40mm | ASTMD648 | 99.0 | °C | |
Vicat Softening Temperature | ASTMD152512 | 110 | °C | |
-- | ISO306/B50 | 110 | °C | |
-- | ISO306/B120 | 113 | °C | |
Heat Deflection Temperature | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 93.0 | °C |
Thermal Conductivity | ISO8302 | 0.20 | W/m/K | |
Ball PressureTest | 75°C | IEC60695-10-2 | Pass |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Hot-wire Ignition | HWI | UL746 | PLC3 | |
High Amp Arc Ignition | HAI | UL746 | PLC0 | |
Comparative Tracking Index | CTI | UL746 | PLC3 | |
Surface Resistivity | IEC60093 | >1.0E+15 | ohms | |
Volume Resistivity | IEC60093 | >1.0E+15 | ohms·cm | |
Dielectric Strength | 0.800mm,in Oil | IEC60243-1 | 35 | KV/mm |
1.60mm,in Oil | IEC60243-1 | 25 | KV/mm | |
3.20mm,in Oil | IEC60243-1 | 17 | KV/mm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 65.0 | J |
Charpy Notched Impact Strength | -30°C7 | ISO179/1eA | 10 | kJ/m² |
23°C8 | ISO179/1eA | 22 | kJ/m² | |
23°C7 | ISO179/1eA | 20 | kJ/m² | |
Notched Izod Impact Strength | -30°C | ASTMD256 | 180 | J/m |
23°C | ASTMD256 | 700 | J/m | |
-30°C9 | ISO180/1A | 10 | kJ/m² | |
-30°C10 | ISO180/1A | 10 | kJ/m² | |
23°C9 | ISO180/1A | 25 | kJ/m² | |
23°C10 | ISO180/1A | 20 | kJ/m² |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
UL flame retardant rating | 0.60mm | UL94 | V-1 | |
0.75mm | UL94 | V-0 | ||
1.5mm | UL94 | 5VB | ||
3.0mm | UL94 | 5VA | ||
Glow Wire Flammability Index | 0.75mm13 | IEC60695-2-12 | 960 | °C |
0.75mm | IEC60695-2-12 | 960 | °C | |
Oxygen Index | ISO4589-2 | 35 | % | |
Glow Wire Ignition Temperature | 0.75mm13 | IEC60695-2-13 | 775 | °C |
1.0mm | IEC60695-2-13 | 825 | °C | |
1.5mm13 | IEC60695-2-13 | 775 | °C | |
3.0mm13 | IEC60695-2-13 | 775 | °C | |
3.0mm | IEC60695-2-13 | 800 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.