Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | TD:4.00mm | 内部方法 | 0.50to0.70 | % |
Modeling Shrinkage | MD:4.00mm | 内部方法 | 0.50to0.70 | % |
Moisture Absorption | 23°C,24hr | ISO62 | 0.20 | % |
Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 18.0 | cm3/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | Yield | ISO527-2/50 | 61.0 | Mpa |
Tensile Stress | Break | ISO527-2/50 | 59.0 | Mpa |
Tensile Strain | Yield | ISO527-2/50 | 6.0 | % |
Tensile Modulus | | ISO527-2/1 | 2400 | Mpa |
Flexural Modulus | | ISO178 | 2180 | Mpa |
Flexural Stress | | ISO178 | 93.0 | Mpa |
Nominal Tensile Strain at Break | | ISO527-2/50 | >50 | % |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 126 | °C |
RTIElec | 1.5mm | UL746 | 130 | °C |
Evolution Calendar intelligent importer | 1.5mm | UL746 | 125 | °C |
RTIStr | 1.5mm | UL746 | 130 | °C |
Linear thermal expansion coefficient | MD | ISO11359-2 | 7E-05 | cm/cm/°C |
Linear thermal expansion coefficient | TD | ISO11359-2 | 7E-05 | cm/cm/°C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Surface Resistivity | | IEC60093 | >1.0E+15 | ohms |
Volume Resistivity | | IEC60093 | >1.0E+15 | ohms·cm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | 23°C | ISO179 | NoBreak | |
optical performance | Test Condition | Test Method | Test Result | Unit |
---|
Transmittance | 3000µm | ASTMD1003 | 49.0 | % |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Flame Rating | 1.0mm | UL94 | V-0 | |
Glow Wire Flammability Index | 1.0mm | IEC60695-2-12 | 930 | °C |
Glow Wire Flammability Index | 3.0mm | IEC60695-2-12 | 960 | °C |
Glow Wire Ignition Temperature | 1.0mm | IEC60695-2-13 | 850 | °C |
Glow Wire Ignition Temperature | 3.0mm | IEC60695-2-13 | 850 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.