Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:--

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	Flow2.0mm	ISO 294	0.50-0.70	%
Modeling Shrinkage	Modeling Shrinkage	垂直2.0mm	ISO 294	0.50-0.70	%
Moisture Absorption	23°C24hr	ISO 62	0.32	%
Moisture Absorption	Moisture Absorption	23℃ 50RH	ISO 62	0.15	%
Melt index	300°C 1.2kg	ISO 1133	10	g/10min
proportion		ISO 1183	1.2	g/cm³

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Charpy Notched Impact Strength	23℃	ISO 179	75	kJ/㎡
Notched Izod Impact Strength	23℃	ISO 180	70	kJ/㎡
Charpy Unnotched Impact Strength	23℃	ISO 179	NB	kJ/㎡
Unnotched Izod Impact Strength	23℃	ISO 180	NB	kJ/㎡
Tensile Modulus	1.0mm/min	ISO 527	2400	Mpa
Tensile Strength	Yield50mm/min	ISO 527	60	Mpa
Tensile Elongation	Yield50mm/min	ISO 527	6	%
Tensile Elongation	Tensile Elongation	Break50mm/mi	ISO 527	150	%
Flexural Modulus	2.0mm/min	ISO 178	2410	Mpa
Flexural Strength	Yield2.0mm/min	ISO 178	97	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	Annealed0.45MPa	ISO 75	144	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	Unannealed1.8MPa	ISO 75	128	°C
Glass Transition Temperature	10℃/min	ISO 11357	149	°C
Vicat Softening Temperature	50℃/hr 50N	ISO 306	149	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface resistance	2.0mm	IEC 60093	10000000000000000	Ω
Comparative Tracking Index		IEC 60112	250	V
Insulation strength	1.0mm	IEC 60243	34	KV/mm
Volume Resistivity	2.0mm	IEC 60093	200000000000000000	Ω.cm
Dissipation Factor?	100Hz	IEC 60250	0.001
Dissipation Factor?	Dissipation Factor?	1MHz	IEC 60250	0.01
Dielectric Constant	100Hz	IEC 60250	3.1
Dielectric Constant	Dielectric Constant	1MHz	IEC 60250	3

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness		ISO 2039	120

optical performance	Test Condition	Test Method	Test Result	Unit
Refractive index of light		ISO 489	1.586
Transmittance		ISO 13468	89	%
秀度	2000㎛	ISO 14782	0.8	%

Flame Rating	Test Condition	Test Method	Test Result	Unit
Fire rating	1.5mm	UL94	HB
Fire rating	Fire rating	3.0mm	UL94	HB
Glow Wire Ignition Temperature	1.5mm	IEC 60695	875	°C
Glow Wire Ignition Temperature	Glow Wire Ignition Temperature	3mm	IEC 60695	960	°C
Oxygen Index		ISO 4589	27	%
Glow Wire Ignition Temperature	1.5mm	IEC 60695	875	°C
Glow Wire Ignition Temperature	Glow Wire Ignition Temperature	3mm	IEC 60695	875	°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.