PC CH8105 1002 F CANGZHOU DAHUA
95
- Unit Price:
- $1761 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 13900MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | Flow2.0mm | ISO 294 | 0.50-0.70 | % |
| 垂直2.0mm | ISO 294 | 0.50-0.70 | % | |
| Moisture Absorption | 23°C24hr | ISO 62 | 0.32 | % |
| 23℃ 50RH | ISO 62 | 0.15 | % | |
| Melt index | 300°C 1.2kg | ISO 1133 | 10 | g/10min |
| proportion | ISO 1183 | 1.2 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 23℃ | ISO 179 | 75 | kJ/㎡ |
| Notched Izod Impact Strength | 23℃ | ISO 180 | 70 | kJ/㎡ |
| Charpy Unnotched Impact Strength | 23℃ | ISO 179 | NB | kJ/㎡ |
| Unnotched Izod Impact Strength | 23℃ | ISO 180 | NB | kJ/㎡ |
| Tensile Modulus | 1.0mm/min | ISO 527 | 2400 | Mpa |
| Tensile Strength | Yield50mm/min | ISO 527 | 60 | Mpa |
| Tensile Elongation | Yield50mm/min | ISO 527 | 6 | % |
| Break50mm/mi | ISO 527 | 150 | % | |
| Flexural Modulus | 2.0mm/min | ISO 178 | 2410 | Mpa |
| Flexural Strength | Yield2.0mm/min | ISO 178 | 97 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | Annealed0.45MPa | ISO 75 | 144 | °C |
| Unannealed1.8MPa | ISO 75 | 128 | °C | |
| Glass Transition Temperature | 10℃/min | ISO 11357 | 149 | °C |
| Vicat Softening Temperature | 50℃/hr 50N | ISO 306 | 149 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistance | 2.0mm | IEC 60093 | 10000000000000000 | Ω |
| Comparative Tracking Index | IEC 60112 | 250 | V | |
| Insulation strength | 1.0mm | IEC 60243 | 34 | KV/mm |
| Volume Resistivity | 2.0mm | IEC 60093 | 200000000000000000 | Ω.cm |
| Dissipation Factor? | 100Hz | IEC 60250 | 0.001 | |
| 1MHz | IEC 60250 | 0.01 | ||
| Dielectric Constant | 100Hz | IEC 60250 | 3.1 | |
| 1MHz | IEC 60250 | 3 |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell Hardness | ISO 2039 | 120 |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Refractive index of light | ISO 489 | 1.586 | ||
| Transmittance | ISO 13468 | 89 | % | |
| 秀度 | 2000㎛ | ISO 14782 | 0.8 | % |
| Flame Rating | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Fire rating | 1.5mm | UL94 | HB | |
| 3.0mm | UL94 | HB | ||
| Glow Wire Ignition Temperature | 1.5mm | IEC 60695 | 875 | °C |
| 3mm | IEC 60695 | 960 | °C | |
| Oxygen Index | ISO 4589 | 27 | % | |
| Glow Wire Ignition Temperature | 1.5mm | IEC 60695 | 875 | °C |
| 3mm | IEC 60695 | 875 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.