PC LEXAN™ EXL4412-7G1A1794 SABIC INNOVATIVE SHANGHAI
53
- Unit Price:
- $5220 USD/MT
- Packaging Specification:
- 25KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.20to0.60 | % |
| Moisture Absorption | Saturation,23°C | ISO62 | 0.12 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.46 | % | |
| Melt Mass-Flow Rate | 300°C/1.2kg | ASTMD1238 | 11 | g/10min |
| Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 10.3 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Elongation | Yield | ASTMD638 | 4.5 | % |
| Tensile Modulus | ASTMD638 | 3300 | Mpa | |
| Tensile Strength | Break | ASTMD638 | 44.0 | Mpa |
| Yield | ASTMD638 | 53.0 | Mpa | |
| Flexural Modulus | 50.0mmSpan | ASTMD790 | 3200 | Mpa |
| Flexural Strength | Yield,50.0mmSpan | ASTMD790 | 95.0 | Mpa |
| Tensile Elongation | Break | ASTMD638 | 20 | % |
| Flexural Modulus | ISO178 | 3300 | Mpa | |
| Flexural Strength | ISO178 | 90.0 | Mpa | |
| Tensile Stress | Yield | ISO527-2/5 | 55.0 | Mpa |
| Break | ISO527-2/5 | 43.0 | Mpa | |
| Tensile Strain | Yield | ISO527-2/5 | 4.5 | % |
| Break | ISO527-2/5 | 13 | % | |
| Tensile Modulus | ISO527-2/1 | 3300 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 135 | °C |
| Linear thermal expansion coefficient | MD：-40to40°C | ASTME831 | 4.1E-05 | cm/cm/°C |
| MD：-40to40°C | ISO11359-2 | 4.1E-05 | cm/cm/°C | |
| TD：-40to40°C | ASTME831 | 6.9E-05 | cm/cm/°C | |
| TD：-40to40°C | ISO11359-2 | 6.9E-05 | cm/cm/°C | |
| Ball PressureTest | 75°C | IEC60695-10-2 | Pass | |
| Vicat Softening Temperature | -- | ISO306/B50 | 144 | °C |
| -- | ISO306/B120 | 146 | °C | |
| ASTMD152510 | 145 | °C | ||
| Heat Deflection Temperature | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 134 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric Strength | 1.60mm,inOil | ASTMD149 | 32 | KV/mm |
| Surface Resistivity | ASTMD257 | 2.9E+17 | ohms | |
| Dielectric Constant | 1MHz | ASTMD150 | 3.04 | |
| 1.90GHz | 内部方法 | 2.95 | ||
| Volume Resistivity | ASTMD257 | 1.8E+17 | ohms·cm | |
| Dissipation Factor? | 1MHz | ASTMD150 | 8.6E-03 | |
| 1.90GHz | 内部方法 | 5.8E-03 |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 40.0 | J |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 15 | kJ/m² |
| 23°C | ISO179/1eA | 25 | kJ/m² | |
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | NoBreak | |
| 23°C | ISO179/1eU | NoBreak | ||
| Notched Izod Impact Strength | -30°C | ISO180/1A | 10 | kJ/m² |
| 23°C | ISO180/1A | 25 | kJ/m² | |
| Unnotched Izod Impact Strength | -30°C | ISO180/1U | NoBreak | |
| 23°C | ISO180/1U | NoBreak |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.