Material Description

Technical Data Sheet

Material Description

Material Properties:High mobility High ductility at low tem
Application Areas:Electronic display Quick charging phone case
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Melt Mass-Flow Rate	300°C/1.2 kg	ASTM D1238	12	g/10 min
Melt Volume flow Rate	300°C/1.2 kg	ISO 1133	10.0	cm3/10min
Modeling Shrinkage	Flow : 3.20 mm	内部方法	0.40 到 0.80	%
Modeling Shrinkage	Modeling Shrinkage	Across Flow : 3.20 mm	内部方法	0.40 到 0.80	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Modulus	-- 2	ASTM D638	2110	Mpa
Tensile Modulus	Tensile Modulus	--	ISO 527-2/1	2140	Mpa
Tensile Elongation	Yield 3	ASTM D638	5.8	%
	Tensile Elongation	Yield	ISO 527-2/50	5.6	%
		Tensile Elongation	Break 3	ASTM D638	110	%
		Tensile Elongation	Tensile Elongation	Break	ISO 527-2/50	110	%
Flexural Modulus	50.0 mm Span 4	ASTM D790	2190	Mpa
Flexural Modulus	Flexural Modulus	-- 5	ISO 178	2180	Mpa
Tensile Strength	Yield 3	ASTM D638	56.0	Mpa
	Tensile Strength	Yield	ISO 527-2/50	57.0	Mpa
		Tensile Strength	Break 3	ASTM D638	62.0	Mpa
		Tensile Strength	Tensile Strength	Break	ISO 527-2/50	60.0	Mpa
Flexural Stress	-- 5, 6	ISO 178	86.0	Mpa
Flexural Stress	Flexural Stress	Yield, 50.0 mm Span 4	ASTM D790	88.0	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Vicat Softening Temperature	--	ISO 306/B50	136	°C
Vicat Softening Temperature	Vicat Softening Temperature	--	ISO 306/B120	138	°C
Linear thermal expansion coefficient	Flow : -40 to 40°C	ASTM E831	6.9E-5	cm/cm/°C
	Linear thermal expansion coefficient	Flow : 23 to 80°C	ISO 11359-2	7.4E-5	cm/cm/°C
		Linear thermal expansion coefficient	Across Flow : -40 to 40°C	ASTM E831	7.3E-5	cm/cm/°C
		Linear thermal expansion coefficient	Linear thermal expansion coefficient	Across Flow : 23 to 80°C	ISO 11359-2	7.6E-5	cm/cm/°C
Deflection Temperature Under Load?	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	134	°C
	Deflection Temperature Under Load?	0.45 MPa, Unannealed, 4.00 mm, 100 mm Span 9	ISO 75-2/Be	131	°C
		Deflection Temperature Under Load?	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	118	°C
		Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span 9	ISO 75-2/Ae	117	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dissipation Factor?	1.10 GHz	ASTM ES7-83	6.0E-3
Surface Resistivity		ASTM D257	> 1.0E+16	ohms
Dielectric Constant	1.10 GHz	ASTM ES7-83	2.78
Volume Resistivity		ASTM D257	> 1.0E+16	ohms·cm
Dielectric Strength	3.20 mm, in Oil	ASTM D149	13	KV/mm

Injection	Test Result	Unit
Drying Temperature	120	°C
Suggested Max Moisture	0.020	%
Processing (Melt) Temp	295 到 315	°C
Mold Temperature	70 到 95	°C
Drying Time	3.0 到 4.0	hr
Suggested Shot Size	40 到 60	%
Rear Temperature	270 到 295	°C
Middle Temperature	280 到 305	°C
Front Temperature	295 到 315	°C
Nozzle Temperature	290 到 310	°C
Back Pressure	0.300 到 0.700	Mpa
Screw Speed	40 到 70	rpm
Vent Depth	0.025 到 0.076	mm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Instrumented Dart Impact	23°C, Total Energy	ASTM D3763	67.0	J
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	29	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	75	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	L -Sale	ASTM D785	83
Rockwell Hardness	Rockwell Hardness	R-Scale	ASTM D785	117

Flammability	Test Condition	Test Method	Test Result	Unit
Glow Wire Flammability Index	1.0 mm	IEC 60695-2-12	960	°C
Oxygen Index		ISO 4589-2	39	%
Glow Wire Ignition Temperature	1.0 mm	IEC 60695-2-13	850	°C
Flame Rating	0.50 mm	UL 94	V-2
	Flame Rating	0.8 mm	UL 94	V-1
		Flame Rating	1.0 mm	UL 94	V-0
			Flame Rating	1.5 mm	UL 94	5VB
			Flame Rating	Flame Rating	3.1 mm	UL 94	5VA

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.