Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | | ISO 294-4 | 0.50 到 0.70 | % |
Melt Volume flow Rate | 300°C/1.2 kg | ISO 1133 | 15.0 | cm3/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Flexural Modulus | | ISO 178 | 2400 | Mpa |
Flexural Stress | | ISO 178 | 90.0 | Mpa |
Tensile Stress | Yield | ISO 527-2/50 | 64.0 | Mpa |
Tensile Stress | Break | ISO 527-2/50 | 70.0 | Mpa |
Tensile Strain | Break | ISO 527-2/50 | 120 | % |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 1.8 MPa, Unannealed | ISO 75-2/A | 128 | °C |
Deflection Temperature Under Load? | 1.8 MPa, Annealed | ISO 75-2/A | 143 | °C |
Vicat Softening Temperature | -- | ISO 306/A50 | 150 | °C |
Vicat Softening Temperature | -- | ISO 306/B50 | 145 | °C |
Coefficient of Linear Thermal Expansion (Flow) | | ISO 11359-2 | 6.0E-5 到 8.0E-5 | cm/cm/°C |
Injection | Test Condition | Test Method | Test Result | Unit |
---|
Drying Time | | | 4.0 | hr |
Rear Temperature | | | 230 到 300 | °C |
Middle Temperature | | | 250 到 310 | °C |
Front Temperature | | | 250 到 300 | °C |
Drying Temperature | | | 120 | °C |
Mold Temperature | | | 70 到 120 | °C |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Flame Rating | 2.5 mm | UL 94 | V-2 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.