Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:--

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	MD:24hr	ASTMD955	0.20到0.40	%
Modeling Shrinkage	Modeling Shrinkage	TD:24hr	ASTMD955	0.20到0.40	%
Moisture Absorption	Saturation,23°C	ISO62	0.070	%
Moisture Absorption	Moisture Absorption	Equilibrium,23°C,50%RH	ISO62	0.030	%
Melt Mass-Flow Rate	300°C/1.2kg	ASTMD1238	17	g/10min
Melt Mass-Flow Rate	Melt Mass-Flow Rate	300°C/2.16kg	ASTMD1238	33	g/10min
Melt Volume flow Rate	300°C/1.2kg	ISO1133	15.0	cm3/10min
Melt Volume flow Rate	Melt Volume flow Rate	300°C/2.16kg	ISO1133	29.0	cm3/10min

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
fracture		ISO527-2/5	112	Mpa
	fracture		ISO527-2/5	2.6	%
		fracture		ISO527-2/5	112	Mpa
		fracture	fracture		ISO527-2/5	2.6	%
Break		ASTMD638	2.7	%
Break	Break		ASTMD638	2.7	%
50.0mm Span		ASTMD790	6150	Mpa
50.0mm Span	50.0mm Span		ASTMD790	6150	Mpa
--5		ISO178	6240	Mpa
--5	--5		ISO178	6240	Mpa
--6		ISO178	165	Mpa
--6	--6		ISO178	165	Mpa
Break		ASTMD638	110	Mpa
Break	Break		ASTMD638	110	Mpa
Break,50.0mm Span		ASTMD790	167	Mpa
Break,50.0mm Span	Break,50.0mm Span		ASTMD790	167	Mpa
--1		ASTMD638	6680	Mpa
--1	--1		ASTMD638	6680	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Linear thermal expansion coefficient	MD:23to80°C	ISO11359-2	2.6E-05	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	TD:23to80°C	ISO11359-2	7.3E-05	cm/cm/°C
Deflection Temperature Under Load?	0.45MPa,Unannealed,3.20mm	ASTMD648	121	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,Unannealed,3.20mm	ASTMD648	116	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric Constant	1.10GHz	内部方法	3.20
	Dielectric Constant	1.90GHz	内部方法	3.20
		Dielectric Constant	5.00GHz	内部方法	3.20
			Dielectric Constant	10.0GHz	内部方法	3.20
			Dielectric Constant	Dielectric Constant	20.0GHz	内部方法	3.20
Dissipation Factor?	1.10GHz	内部方法	6.3E-03
	Dissipation Factor?	1.90GHz	内部方法	6.3E-03
		Dissipation Factor?	5.00GHz	内部方法	6.4E-03
			Dissipation Factor?	10.0GHz	内部方法	6.7E-03
			Dissipation Factor?	Dissipation Factor?	20.0GHz	内部方法	6.5E-03

Impact Properties	Test Condition	Test Method	Test Result	Unit
Unnotched Izod Impact Strength	23°C	ASTMD4812	720	J/m
Charpy Notched Impact Strength	23°C	ISO179/1eA	14	kJ/m²
Instrumented Dart Impact	23°C,EnergyatPeakLoad	ASTMD3763	22.0	J
Charpy Unnotched Impact Strength	23°C	ISO179/1eU	51	kJ/m²

Flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.500mm	UL94	V-1
	UL flame retardant rating	0.600mm	UL94	V-0
	UL flame retardant rating	UL flame retardant rating	0.300mm	UL94	V-2

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.