PC LEXAN™ EXL9330-7T7D185 SABIC INNOVATIVE SHANGHAI

Unit Price:
$5111 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
20.5MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:UV resistance Toughening Flame retardant
Application Areas:Thin walled products food Lighting fixtures
Color:--
Grade:--

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	Flow : 3.20 mm	内部方法	0.40 到 0.80	%
Modeling Shrinkage	Modeling Shrinkage	Across Flow : 3.20 mm	内部方法	0.40 到 0.80	%
Moisture Absorption	Saturation, 23°C	ISO 62	0.35	%
Moisture Absorption	Moisture Absorption	Equilibrium, 23°C, 50% RH	ISO 62	0.15	%
Outdoor Suitability		UL 746C	f1
Melt Mass-Flow Rate	300°C/1.2 kg	ASTM D1238	10	g/10 min
Melt Volume flow Rate	300°C/1.2 kg	ISO 1133	9.00	cm3/10min

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Stress	-- 5, 6	ISO 178	85.0	Mpa
Flexural Stress	Flexural Stress	Yield, 50.0 mm Span 4	ASTM D790	88.0	Mpa
Tensile Strength	Yield 3	ASTM D638	58.0	Mpa
	Tensile Strength	Yield	ISO 527-2/50	55.0	Mpa
		Tensile Strength	Break 3	ASTM D638	61.0	Mpa
		Tensile Strength	Tensile Strength	Break	ISO 527-2/50	60.0	Mpa
Tensile Modulus	-- 2	ASTM D638	2100	Mpa
Tensile Modulus	Tensile Modulus	--	ISO 527-2/1	2100	Mpa
Tensile Elongation	Yield 3	ASTM D638	6.0	%
	Tensile Elongation	Yield	ISO 527-2/50	6.0	%
		Tensile Elongation	Break 3	ASTM D638	130	%
		Tensile Elongation	Tensile Elongation	Break	ISO 527-2/50	130	%
Flexural Modulus	50.0 mm Span 4	ASTM D790	2060	Mpa
Flexural Modulus	Flexural Modulus	-- 5	ISO 178	2200	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Vicat Softening Temperature	--	ASTM D152512, ISO 306/B12012	142	°C
Vicat Softening Temperature	Vicat Softening Temperature	--	ISO 306/B50	140	°C
Linear thermal expansion coefficient	Flow : -40 to 40°C	ASTM E831	6.7E-5	cm/cm/°C
	Linear thermal expansion coefficient	Flow : 23 to 80°C	ISO 11359-2	7.2E-5	cm/cm/°C
		Linear thermal expansion coefficient	Across Flow : -40 to 40°C	ASTM E831	6.7E-5	cm/cm/°C
		Linear thermal expansion coefficient	Linear thermal expansion coefficient	Across Flow : 23 to 80°C	ISO 11359-2	7.7E-5	cm/cm/°C
RTI		UL 746	120	°C
RTI Imp		UL 746	115	°C
RTI Elec		UL 746	125	°C
Deflection Temperature Under Load?	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	134	°C
	Deflection Temperature Under Load?	0.45 MPa, Unannealed, 4.00 mm, 100 mm Span 11	ISO 75-2/Be	135	°C
		Deflection Temperature Under Load?	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	120	°C
			Deflection Temperature Under Load?	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	124	°C
			Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span 11	ISO 75-2/Ae	124	°C
Ball PressureTest	123 to 127°C	IEC 60695-10-2	通过

Electrical performance	Test Condition	Test Method	Test Result	Unit
Comparative Tracking Index		UL 746	PLC 3
Hot-wire Ignition		UL 746	PLC 1
Dielectric Strength	3.20 mm, in Oil	ASTM D149	17	KV/mm
Dielectric Strength	Dielectric Strength	3.20 mm, in Oil	IEC 60243-1	16	KV/mm
Comparative Tracking Index		IEC 60112	225	V
Dissipation Factor?	50 Hz	ASTM D150	2.4E-3
	Dissipation Factor?	60 Hz	ASTM D150	2.4E-3
		Dissipation Factor?	1 MHz	ASTM D150, IEC 60250	8.5E-3
			Dissipation Factor?	50 Hz	IEC 60250	1.0E-3
			Dissipation Factor?	Dissipation Factor?	60 Hz	IEC 60250	1.0E-3
Surface Resistivity		IEC 60093	> 1.0E+15	ohms
Dielectric Constant	60 Hz	ASTM D150	2.95
	Dielectric Constant	50 kHz	ASTM D150	2.95
		Dielectric Constant	1 MHz	ASTM D150	2.90
			Dielectric Constant	50 Hz	IEC 60250	2.60
				Dielectric Constant	60 Hz	IEC 60250	2.60
				Dielectric Constant	Dielectric Constant	1 MHz	IEC 60250	2.70
Volume Resistivity		IEC 60093	> 1.0E+15	ohms·cm
High Amp Arc Ignition		UL 746	PLC 0

Injection	Test Result	Unit
Drying Temperature	120	°C
Suggested Max Moisture	0.020	%
Processing (Melt) Temp	295 到 315	°C
Mold Temperature	70 到 95	°C
Drying Time	3.0 到 4.0	hr
Suggested Shot Size	40 到 60	%
Rear Temperature	215 到 295	°C
Middle Temperature	280 到 305	°C
Front Temperature	295 到 315	°C
Nozzle Temperature	290 到 310	°C
Back Pressure	0.300 到 0.700	Mpa
Screw Speed	40 到 70	rpm
Vent Depth	0.025 到 0.076	mm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Instrumented Dart Impact	23°C, Total Energy	ASTM D3763	52.0	J
Unnotched Izod Impact Strength	-30°C	ISO 180/1U	无断裂
Unnotched Izod Impact Strength	Unnotched Izod Impact Strength	23°C	ISO 180/1U	无断裂
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	60	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	75	kJ/m²
Charpy Unnotched Impact Strength	-30°C	ISO 179/1eU	无断裂
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO 179/1eU	无断裂

hardness	Test Condition	Test Method	Test Result	Unit
Ball Indentation Hardness	H 358/30	ISO 2039-1	90.0	Mpa

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating	1.5 mm	UL 94	V-0
Flame Rating	Flame Rating	3.0 mm	UL 94	5VA
Glow Wire Flammability Index	1.0 mm	IEC 60695-2-12	960	°C
Oxygen Index		ISO 4589-2	35	%
Glow Wire Ignition Temperature	1.0 mm	IEC 60695-2-13	825	°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.