PC Makrolon® 2858 550115 COVESTRO SHANGHAI

173

Unit Price:
$3505 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
149.3MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Medium viscosity
Application Areas:Non specific food Nursing supplies Medical supplies
Color:--
Grade:--

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	TD	ISO2577	0.60to0.80	%
	Modeling Shrinkage	MD	ISO2577	0.60to0.80	%
		Modeling Shrinkage	TD:2.00mm3	ISO294-4	0.75	%
		Modeling Shrinkage	Modeling Shrinkage	MD:2.00mm3	ISO294-4	0.70	%
Moisture Absorption	Saturation,23°C	ISO62	0.30	%
Moisture Absorption	Moisture Absorption	Equilibrium,23°C,50%RH	ISO62	0.12	%
Melt Mass-Flow Rate	300°C/1.2kg	ISO1133	10	g/10min
Melt Volume flow Rate	300°C/1.2kg	ISO1133	9.00	cm3/10min
Density / Specific Gravity	23°C	ISO1183	1.20	g/cm³
Apparent Density		ISO60	0.66	g/cm³

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Nominal Tensile Strain at Break	23°C	ISO527-2/50	>50	%
Flexural Strain	23°C	ISO178	7.1	%
Flexural Stress	3.5%Strain,23°C	ISO178	73.0	Mpa
Flexural Stress	Flexural Stress	23°C	ISO178	97.0	Mpa
Flexural Modulus	23°C	ISO178	2400	Mpa
Tensile Creep Modulus	1hr	ISO899-1	2200	Mpa
Tensile Stress	Yield,23°C	ISO527-2/50	66.0	Mpa
Tensile Stress	Tensile Stress	Break,23°C	ISO527-2/50	70.0	Mpa
Tensile Strain	Yield,23°C	ISO527-2/50	6.1	%
Tensile Strain	Tensile Strain	Break,23°C	ISO527-2/50	130	%
Tensile Creep Modulus	1000hr	ISO899-1	1900	Mpa
Tensile Modulus	23°C	ISO527-2/1	2400	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	0.45MPa,Unannealed	ISO75-2/B	137	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,Unannealed	ISO75-2/A	125	°C
Vicat Softening Temperature	--	ISO306/B50	145	°C
Vicat Softening Temperature	Vicat Softening Temperature	--	ISO306/B120	146	°C
Linear thermal expansion coefficient	MD：23to55°C	ISO11359-2	6.5E-05	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	TD：23to55°C	ISO11359-2	6.5E-05	cm/cm/°C
Ball PressureTest	136°C	IEC60695-10-2	Pass
Glass Transition Temperature		ISO11357-2	145	°C
Thermal Conductivity	23°C	ISO8302	0.20	W/m/K

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric Strength	23°C,1.00mm	IEC60243-1	34	KV/mm
Dissipation Factor?	23°C,100Hz	IEC60250	5E-04
Dissipation Factor?	Dissipation Factor?	23°C,1MHz	IEC60250	9E-03
Relative Permittivity	23°C,100Hz	IEC60250	3.10
Relative Permittivity	Relative Permittivity	23°C,1MHz	IEC60250	3.00
Comparative Tracking Index	SolutionA	IEC60112	250	V
Surface Resistivity		IEC60093	1E+16	ohms
Volume Resistivity	23°C	IEC60093	1E+16	ohms·cm

Film	Test Condition	Test Method	Test Result	Unit
Gas Permeation	CarbonDioxide:23°C,100.0µm	ISO2556	3800	cm³/m²/bar/24hr
	Gas Permeation	Nitrogen:23°C,100.0µm	ISO2556	120	cm³/m²/bar/24hr
	Gas Permeation	Gas Permeation	Oxygen:23°C,100.0µm	ISO2556	650	cm³/m²/bar/24hr

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Notched Impact Strength	-30°C,Complete Break	ISO7391	16	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C,Partial Break	ISO7391	75	kJ/m²
Multi-Axial Instrumented Impact Energy	-30°C	ISO6603-2	65.0	J
Multi-Axial Instrumented Impact Energy	Multi-Axial Instrumented Impact Energy	23°C	ISO6603-2	60.0	J
Notched Izod Impact Strength	-30°C,Complete Break	ISO7391	15	kJ/m²
Notched Izod Impact Strength	Notched Izod Impact Strength	23°C,Partial Break	ISO7391	70	kJ/m²
Multi-Axial Instrumented Impact Peak Force	-30°C	ISO6603-2	6300	N
Multi-Axial Instrumented Impact Peak Force	Multi-Axial Instrumented Impact Peak Force	23°C	ISO6603-2	5400	N
Charpy Unnotched Impact Strength	-60°C	ISO179/1eU	NoBreak
	Charpy Unnotched Impact Strength	-30°C	ISO179/1eU	NoBreak
	Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO179/1eU	NoBreak

hardness	Test Condition	Test Method	Test Result	Unit
Ball Indentation Hardness		ISO2039-1	115	Mpa

optical performance	Test Condition	Test Method	Test Result	Unit
RefractiveIndex11		ISO489	1.586
Transmittance	1000µm	ISO13468-2	89.0	%
	Transmittance	2000µm	ISO13468-2	89.0	%
		Transmittance	3000µm	ISO13468-2	88.0	%
		Transmittance	Transmittance	4000µm	ISO13468-2	87.0	%
Haze	3000µm	ISO14782	<0.80	%

Flammability	Test Condition	Test Method	Test Result	Unit
FlashIgnition		ASTMD1929	480	°C
Oxygen Index		ISO4589-2	28	%
SelfIgnition		ASTMD1929	550	°C
Glow Wire Flammability Index	1.5mm	IEC60695-2-12	850	°C
Glow Wire Flammability Index	Glow Wire Flammability Index	3.0mm	IEC60695-2-12	930	°C
Glow Wire Ignition Temperature	0.75mm	IEC60695-2-13	875	°C
	Glow Wire Ignition Temperature	1.5mm	IEC60695-2-13	875	°C
	Glow Wire Ignition Temperature	Glow Wire Ignition Temperature	3.0mm	IEC60695-2-13	900	°C

Supplementary information	Test Condition	Test Method	Test Result	Unit
ISO Shortname			ISO7391-PC,MR,(,,)-09-9

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.