PC LNP™ THERMOCOMP™ DX11355-BKNAT SABIC INNOVATIVE NANSHA

Unit Price:
$8835 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
98.1MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Thermal stability High mobility
Application Areas:Electronic and electrical Automotive components
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	Flow : 24hr		0.5	%
Modeling Shrinkage	Modeling Shrinkage	Across Flow : 24hr		0.5	%
Melt Mass-Flow Rate	300°C/1.2 kg	ASTM D1238	12	g/10 min
Moisture Absorption	24 hr, 23°C, 50% RH	ASTM D570	0.01	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Modulus	50.0 mm Span	ASTM D790	2400	Mpa
Tensile Modulus		ASTM D638	2600	Mpa
Tensile Elongation	Yield		5.4	%
Tensile Elongation	Tensile Elongation	Break		70	%
Tensile Strength	Yield		58	Mpa
Tensile Strength	Tensile Strength	Break		52	Mpa
Flexural Strength	Yield, 50.0 mm Span		90	Mpa
Flexural Strength	Flexural Strength	Break, 50.0 mm Span		89	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load (1.8Mpa Unannealed)		ASTM D648	114	°C
Linear thermal expansion coefficient	Flow : -40 to 40°C		0.000062	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	垂直 : -40 to 40°C		0.000067	cm/cm/°C
RTI		UL 746B	80	°C
RTI Imp		UL 746B	80	°C
RTI Elec		UL 746B	80	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Relative Permittivity	1.00 GHz	IEC 60250	2.92
Dissipation Factor	1.00 GHz	IEC 60250	0.007

Injection	Test Result	Unit
Drying Temperature	100 到 110	°C
Suggested Max Moisture	0.02	%
Processing (Melt) Temp	275 到 300	°C
Mold Temperature	60 到 90	°C
Drying Time	3.0 到 4.0	hr
Suggested Shot Size	30 到 80	%
Rear Temperature	250 到 290	°C
Middle Temperature	255 到 295	°C
Front Temperature	260 到 300	°C
Nozzle Temperature	275 到 300	°C
Back Pressure	0.300 到 0.700	Mpa
Screw Speed	40 到 70	rpm
Vent Depth	0.038 到 0.076	mm
Hopper Temperature	60 到 80	°C

Impact Properties	Test Condition	Test Method	Test Result	Unit
Unnotched Izod Impact Strength		ASTM D4812	2100	J/m

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating	> 0.60 mm	UL 94	V-0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.