PC LNP™ THERMOCOMP™ D251-7A1D310 SABIC INNOVATIVE NANSHA
75
- Unit Price:
- $6170 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Non chloro non bromine fl Glass fiber reinforced
- Application Areas:Electronic and Electrical Electronic display
- Color:--
- Grade:--
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | MD:24hr | ASTMD955 | 0.20到0.40 | % |
| TD:24hr | ASTMD955 | 0.20到0.40 | % | |
| Moisture Absorption | Saturation,23°C | ISO62 | 0.070 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.030 | % | |
| Melt Mass-Flow Rate | 300°C/1.2kg | ASTMD1238 | 17 | g/10min |
| 300°C/2.16kg | ASTMD1238 | 33 | g/10min | |
| Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 15.0 | cm3/10min |
| 300°C/2.16kg | ISO1133 | 29.0 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| fracture | ISO527-2/5 | 112 | Mpa | |
| ISO527-2/5 | 2.6 | % | ||
| ISO527-2/5 | 112 | Mpa | ||
| ISO527-2/5 | 2.6 | % | ||
| Break | ASTMD638 | 2.7 | % | |
| ASTMD638 | 2.7 | % | ||
| 50.0mm Span | ASTMD790 | 6150 | Mpa | |
| ASTMD790 | 6150 | Mpa | ||
| --5 | ISO178 | 6240 | Mpa | |
| ISO178 | 6240 | Mpa | ||
| --6 | ISO178 | 165 | Mpa | |
| ISO178 | 165 | Mpa | ||
| Break | ASTMD638 | 110 | Mpa | |
| ASTMD638 | 110 | Mpa | ||
| Break,50.0mm Span | ASTMD790 | 167 | Mpa | |
| ASTMD790 | 167 | Mpa | ||
| --1 | ASTMD638 | 6680 | Mpa | |
| ASTMD638 | 6680 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear thermal expansion coefficient | MD:23to80°C | ISO11359-2 | 2.6E-05 | cm/cm/°C |
| TD:23to80°C | ISO11359-2 | 7.3E-05 | cm/cm/°C | |
| Deflection Temperature Under Load? | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 121 | °C |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 116 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric Constant | 1.10GHz | 内部方法 | 3.20 | |
| 1.90GHz | 内部方法 | 3.20 | ||
| 5.00GHz | 内部方法 | 3.20 | ||
| 10.0GHz | 内部方法 | 3.20 | ||
| 20.0GHz | 内部方法 | 3.20 | ||
| Dissipation Factor? | 1.10GHz | 内部方法 | 6.3E-03 | |
| 1.90GHz | 内部方法 | 6.3E-03 | ||
| 5.00GHz | 内部方法 | 6.4E-03 | ||
| 10.0GHz | 内部方法 | 6.7E-03 | ||
| 20.0GHz | 内部方法 | 6.5E-03 |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Unnotched Izod Impact Strength | 23°C | ASTMD4812 | 720 | J/m |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 14 | kJ/m² |
| Instrumented Dart Impact | 23°C,EnergyatPeakLoad | ASTMD3763 | 22.0 | J |
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 51 | kJ/m² |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.500mm | UL94 | V-1 | |
| 0.600mm | UL94 | V-0 | ||
| 0.300mm | UL94 | V-2 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.