PC LEXAN™ LUX7630C-NAT SABIC INNOVATIVE NANSHA

Unit Price:
$6303 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
15.9MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Flame retardant
Application Areas:Electronic display Lighting applications
Color:--
Grade:--

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	Flow : 3.20 mm	内部方法	0.55 到 0.75	%
Modeling Shrinkage	Modeling Shrinkage	Across Flow : 3.20 mm	内部方法	0.60 到 0.80	%
Moisture Absorption	Saturation, 23°C	ISO 62	0.14	%
Moisture Absorption	Moisture Absorption	Equilibrium, 23°C, 50% RH	ISO 62	0.11	%
Outdoor Suitability		UL 746C	f1
Melt Mass-Flow Rate	300°C/1.2 kg	ASTM D1238	5.0	g/10 min
Melt Volume flow Rate	300°C/1.2 kg	ISO 1133	5.00	cm3/10min

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Stress	-- 5, 6	ISO 178	103	Mpa
Flexural Stress	Flexural Stress	Yield, 50.0 mm Span 4	ASTM D790	106	Mpa
Tensile Strength	Yield 3	ASTM D638	68.0	Mpa
	Tensile Strength	Yield	ISO 527-2/50	67.0	Mpa
		Tensile Strength	Break 3	ASTM D638	52.0	Mpa
		Tensile Strength	Tensile Strength	Break	ISO 527-2/50	52.0	Mpa
Tensile Modulus	-- 2	ASTM D638	2500	Mpa
Tensile Modulus	Tensile Modulus	--	ISO 527-2/1	2400	Mpa
Tensile Elongation	Yield 3	ASTM D638	6.0	%
	Tensile Elongation	Yield	ISO 527-2/50	6.0	%
		Tensile Elongation	Break 3	ASTM D638	51	%
		Tensile Elongation	Tensile Elongation	Break	ISO 527-2/50	23	%
Flexural Modulus	50.0 mm Span 4	ASTM D790	2400	Mpa
Flexural Modulus	Flexural Modulus	-- 5	ISO 178	2500	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Vicat Softening Temperature	--	ASTM D152510	136	°C
	Vicat Softening Temperature	--	ISO 306/B50	137	°C
	Vicat Softening Temperature	Vicat Softening Temperature	--	ISO 306/B120	139	°C
Linear thermal expansion coefficient	Flow : -40 to 40°C	ASTM E831	6.6E-5	cm/cm/°C
	Linear thermal expansion coefficient	Flow : 23 to 80°C	ISO 11359-2	7.2E-5	cm/cm/°C
		Linear thermal expansion coefficient	Across Flow : -40 to 40°C	ASTM E831	7.0E-5	cm/cm/°C
		Linear thermal expansion coefficient	Linear thermal expansion coefficient	Across Flow : 23 to 80°C	ISO 11359-2	7.6E-5	cm/cm/°C
RTI		UL 746	125	°C
RTI Imp		UL 746	120	°C
RTI Elec		UL 746	125	°C
Deflection Temperature Under Load?	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	131	°C
	Deflection Temperature Under Load?	0.45 MPa, Unannealed, 4.00 mm, 100 mm Span 9	ISO 75-2/Be	131	°C
		Deflection Temperature Under Load?	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	120	°C
		Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span 9	ISO 75-2/Ae	120	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dissipation Factor?	1.10 GHz	ASTM ES7-83	5.8E-3
Dielectric Constant	1.10 GHz	ASTM ES7-83	2.79

Injection	Test Result	Unit
Drying Temperature	120	°C
Suggested Max Moisture	0.020	%
Processing (Melt) Temp	290 到 310	°C
Mold Temperature	70 到 95	°C
Drying Time	3.0 到 4.0	hr
Suggested Shot Size	40 到 60	%
Rear Temperature	265 到 290	°C
Middle Temperature	275 到 300	°C
Front Temperature	290 到 310	°C
Nozzle Temperature	280 到 305	°C
Back Pressure	0.300 到 0.700	Mpa
Screw Speed	40 到 70	rpm
Vent Depth	0.025 到 0.076	mm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Instrumented Dart Impact	23°C, Total Energy	ASTM D3763	66.0	J
Unnotched Izod Impact Strength	-30°C	ASTM D4812, ISO 180/1U	无断裂
Unnotched Izod Impact Strength	Unnotched Izod Impact Strength	23°C	ASTM D4812, ISO 180/1U	无断裂
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	9.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	10	kJ/m²
Charpy Unnotched Impact Strength	-30°C	ISO 179/1eU	无断裂
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO 179/1eU	无断裂

optical performance	Test Condition	Test Method	Test Result	Unit
Transmittance	2540 µm	ASTM D1003	> 88.0	%

Flammability	Test Condition	Test Method	Test Result	Unit
Glow Wire Flammability Index	1.0 mm	IEC 60695-2-12	960	°C
Oxygen Index		ISO 4589-2	45	%
Glow Wire Ignition Temperature	1.0 mm	IEC 60695-2-13	875	°C
Flame Rating	0.40 mm	UL 94	V-2
	Flame Rating	1.0 mm	UL 94	V-0
	Flame Rating	Flame Rating	3.0 mm	UL 94	5VA

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.