Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | TD:3.20mm | | 0.40to0.60 | % |
| Modeling Shrinkage | MD:3.20mm | | 0.30to0.50 | % |
| Modeling Shrinkage | 吸水率(Saturation,23°C) | | 0.14 | % |
| Melt Mass-Flow Rate | 300°C/1.2kg | ISO1133 | 12 | g/10min |
| Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 11.0 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Flexural Stress | | ISO178 | 120 | Mpa |
| Tensile Stress | Break | ISO527-2 | 75.0 | Mpa |
| Tensile Strain | Break | ISO527-2 | 3.4 | % |
| Tensile Modulus | | ISO527-2 | 4200 | Mpa |
| Flexural Modulus | | ISO178 | 3500 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 139 | °C |
| Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 134 | °C |
| Linear thermal expansion coefficient | MD | ISO11359-2 | 4E-05 | cm/cm/°C |
| Linear thermal expansion coefficient | TD | ISO11359-2 | 6.7E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Comparative Tracking Index | CTI | UL746 | PLC3 | |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | 23°C | ISO179 | 68 | kJ/m² |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 0.40mm | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.