Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melt Mass-Flow Rate | 300°C/1.2 kg | ASTM D1238 | 18 | g/10 min |
Modeling Shrinkage - Flow | 23°C, 3.20 mm, Injection | ASTM D955 | 0.20 到 0.40 | % |
Density / Specific Gravity | | ASTM D792 | 1.25 | g/cm³ |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Flexural Modulus | 23°C, 3.20 mm, Injection | ASTM D790 | 3920 | Mpa |
Flexural Strength | 23°C, 3.20 mm, Injection | ASTM D790 | 137 | Mpa |
Tensile Strength | Yield, 23°C, 3.20 mm, Injection | ASTM D638 | 83.4 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
RTI | | UL 746 | 105 | °C |
RTI Imp | | UL 746 | 90.0 | °C |
RTI Elec | | UL 746 | 120 | °C |
Deflection Temperature Under Load? | 1.8 MPa, Unannealed, 6.40 mm, Injection | ASTM D648 | 138 | °C |
Injection | Test Condition | Test Method | Test Result | Unit |
---|
Drying Time | | | 3.0 到 5.0 | hr |
Rear Temperature | | | 270 到 300 | °C |
Middle Temperature | | | 280 到 310 | °C |
Front Temperature | | | 290 到 330 | °C |
Nozzle Temperature | | | 290 到 330 | °C |
Back Pressure | | | 0.981 到 3.92 | Mpa |
Screw Speed | | | 40 到 70 | rpm |
Drying Temperature | | | 100 到 200 | °C |
Suggested Max Moisture | | | 0.020 | % |
Processing (Melt) Temp | | | 300 到 340 | °C |
Mold Temperature | | | 90 到 120 | °C |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Notched Izod Impact Strength | 23°C, 3.20 mm, Injection | ASTM D256 | 78 | J/m |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | R-Scale, 23°C, Injection | ASTM D785 | 124 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Flame Rating | 1.5 mm, ALL | UL 94 | V-0 | |
Flame Rating | 3.0 mm, ALL | UL 94 | V-0 5VA | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.