PC Makrolon® 9425 000000 COVESTRO SHANGHAI

Unit Price:
$3426 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
34MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	TD	ISO2577	0.30to0.50	%
	Modeling Shrinkage	MD	ISO2577	0.30to0.50	%
		Modeling Shrinkage	TD:2.00mm3	ISO294-4	0.45	%
		Modeling Shrinkage	Modeling Shrinkage	MD:2.00mm3	ISO294-4	0.35	%
Moisture Absorption	Saturation,23°C	ISO62	0.24	%
Moisture Absorption	Moisture Absorption	Equilibrium,23°C,50%RH	ISO62	0.10	%
Melt Mass-Flow Rate	300°C/1.2kg	ISO1133	6.0	g/10min
Melt Volume flow Rate	300°C/1.2kg	ISO1133	5.00	cm3/10min
Density / Specific Gravity	23°C	ISO1183	1.34	g/cm³
Apparent Density		ISO60	0.64	g/cm³

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Strain	23°C	ISO178	3.5	%
Tensile Creep Modulus	1hr	ISO899-1	5700	Mpa
Flexural Stress	23°C	ISO178	135	Mpa
Flexural Modulus	23°C	ISO178	5500	Mpa
Tensile Stress	Break,23°C	ISO527-2/5	86.0	Mpa
Tensile Strain	Break,23°C	ISO527-2/5	2.6	%
Tensile Creep Modulus	1000hr	ISO899-1	5200	Mpa
Tensile Modulus	23°C	ISO527-2/1	5800	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	0.45MPa,Unannealed	ISO75-2/B	142	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,Unannealed	ISO75-2/A	138	°C
RTIElec	1.5mm	UL746	130	°C
Evolution Calendar intelligent importer	1.5mm	UL746	125	°C
RTIStr	1.5mm	UL746	125	°C
Vicat Softening Temperature	--	ISO306/B50	146	°C
Vicat Softening Temperature	Vicat Softening Temperature	--	ISO306/B120	148	°C
Linear thermal expansion coefficient	MD：23to55°C	ISO11359-2	3E-05	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	TD：23to55°C	ISO11359-2	6.5E-05	cm/cm/°C
Thermal Conductivity	23°C	ISO8302	0.23	W/m/K
Ball PressureTest	136°C	IEC60695-10-2	Pass

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric Strength	23°C,1.00mm	IEC60243-1	36	KV/mm
Relative Permittivity	23°C,100Hz	IEC60250	3.30
Relative Permittivity	Relative Permittivity	23°C,1MHz	IEC60250	3.30
Comparative Tracking Index	SolutionA	IEC60112	175	V
Comparative Tracking Index	Comparative Tracking Index	SolutionB	IEC60112	125	V
Dissipation Factor?	23°C,100Hz	IEC60250	1E-03
Dissipation Factor?	Dissipation Factor?	23°C,1MHz	IEC60250	9E-03
Surface Resistivity		IEC60093	1E+16	ohms
Volume Resistivity	23°C	IEC60093	1E+16	ohms·cm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Unnotched Impact Strength	-30°C,Complete Break	ISO179/1eU	50	kJ/m²
	Charpy Unnotched Impact Strength	23°C,Complete Break	ISO179/1eU	40	kJ/m²
	Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	-60°C,CompleteBreak	ISO179/1eU	50	kJ/m²
Multi-Axial Instrumented Impact Energy	-30°C	ISO6603-2	5.00	J
Multi-Axial Instrumented Impact Energy	Multi-Axial Instrumented Impact Energy	23°C	ISO6603-2	5.00	J
CharpyNotchedImpactStrength6	23°C,CompleteBreak	ISO7391	8.0	kJ/m²
Notched Izod Impact Strength	23°C,CompleteBreak	ISO7391	8.0	kJ/m²
Multi-Axial Instrumented Impact Peak Force	-30°C	ISO6603-2	900	N
Multi-Axial Instrumented Impact Peak Force	Multi-Axial Instrumented Impact Peak Force	23°C	ISO6603-2	900	N

hardness	Test Condition	Test Method	Test Result	Unit
Ball Indentation Hardness		ISO2039-1	148	Mpa

Flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	3.0mm	UL94	5VA
	UL flame retardant rating	0.50mm	UL94	V-2
	UL flame retardant rating	UL flame retardant rating	1.5mm	UL94	V-0
Glow Wire Flammability Index	0.75mm	IEC60695-2-12	960	°C
	Glow Wire Flammability Index	1.5mm	IEC60695-2-12	960	°C
	Glow Wire Flammability Index	Glow Wire Flammability Index	3.0mm	IEC60695-2-12	960	°C
Oxygen Index		ISO4589-2	35	%
Glow Wire Ignition Temperature	0.75mm	IEC60695-2-13	875	°C
	Glow Wire Ignition Temperature	1.5mm	IEC60695-2-13	875	°C
	Glow Wire Ignition Temperature	Glow Wire Ignition Temperature	3.0mm	IEC60695-2-13	875	°C
FMVSS Flammability	>1.00mm	ISO3795	passed
FlashIgnition		ASTMD1929	470	°C
Needle Flame Test	MethodF:1.50mm	IEC60695-11-5	2.0	min
	Needle Flame Test	MethodF:2.00mm	IEC60695-11-5	2.0	min
		Needle Flame Test	MethodF:3.00mm	IEC60695-11-5	2.0	min
			Needle Flame Test	MethodK:1.50mm	IEC60695-11-5	1.0	min
				Needle Flame Test	MethodK:2.00mm	IEC60695-11-5	2.0	min
				Needle Flame Test	Needle Flame Test	MethodK:3.00mm	IEC60695-11-5	2.0	min
SelfIgnition		ASTMD1929	550	°C
ApplicationofFlamefromSmallBurner	2.00mm	DIN4102	B2
ApplicationofFlamefromSmallBurner	ApplicationofFlamefromSmallBurner	MethodKandF:2.00mm	DIN53438-1,-3	K1,F1

Supplementary information	Test Condition	Test Method	Test Result	Unit
ISO Shortname			ISO7391-PC,MFR,(,,)-05-3,GF20
ElectrolyticalCorrosion	23°C	IEC60426	A1

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.