Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | MD1 | 内部方法 | 0.50到0.70 | % |
Moisture Absorption | Saturation,23°C | ISO62 | 0.35 | % |
Moisture Absorption | Equilibrium,23°C,50%RH | ISO62 | 0.15 | % |
Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 18.0 | cm3/10min |
Outdoor Suitability | | UL746C | f1 | |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Flexural Stress | | ISO178 | 90.0 | Mpa |
Tensile Stress | Yield | ISO527-2/50 | 62.0 | Mpa |
Tensile Stress | Break | ISO527-2/50 | 69.0 | Mpa |
Tensile Strain | Yield | ISO527-2/50 | 6.0 | % |
Tensile Strain | Break | ISO527-2/50 | 100 | % |
Tensile Modulus | | ISO527-2/1 | 2350 | Mpa |
Taber Abrasion Resistance | 1000Cycles,1000g,CS-17Wheel | 内部方法 | 10.0 | mg |
Flexural Modulus | | ISO178 | 2300 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
0.45MPa, Unannealed,100mm Span | | ISO75-2/Be | 133 | °C |
1.8MPa, Unannealed,100mm Span | | ISO75-2/Ae | 122 | °C |
Linear thermal expansion coefficient | MD:23to80°C | ISO11359-2 | 7E-05 | cm/cm/°C |
RTIElec | | UL746 | 130 | °C |
Evolution Calendar intelligent importer | | UL746 | 125 | °C |
Thermal Conductivity | | ISO8302 | 0.20 | W/m/K |
RTI | | UL746 | 125 | °C |
Ball PressureTest | 125°C | IEC60695-10-2 | Pass | |
-- | | ISO306/B50 | 140 | °C |
-- | | ISO306/B120 | 141 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dissipation Factor? | 50Hz | IEC60250 | 1E-03 | |
Dissipation Factor? | 60Hz | IEC60250 | 1E-03 | |
Dissipation Factor? | 1MHz | IEC60250 | 0.010 | |
Relative Permittivity | 50Hz | IEC60250 | 2.70 | |
Relative Permittivity | 60Hz | IEC60250 | 2.70 | |
Relative Permittivity | 1MHz | IEC60250 | 2.70 | |
Comparative Tracking Index | | IEC60112 | 250 | V |
Surface Resistivity | | IEC60093 | >1.0E+15 | ohms |
Volume Resistivity | | IEC60093 | >1.0E+15 | ohms·cm |
Dielectric Strength | 3.20mm,in Oil | IEC60243-1 | 17 | KV/mm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 无断裂 | |
Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 无断裂 | |
Notched Izod Impact Strength | -30°C | ISO180/1A | 15 | kJ/m² |
Notched Izod Impact Strength | 23°C | ISO180/1A | 65 | kJ/m² |
Unnotched Izod Impact Strength | -30°C | ISO180/1U | 无断裂 | |
Unnotched Izod Impact Strength | 23°C | ISO180/1U | 无断裂 | |
Charpy Notched Impact Strength | -30°C | ISO179/1eA | 12 | kJ/m² |
Charpy Notched Impact Strength | 23°C | ISO179/1eA | 65 | kJ/m² |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Ball Indentation Hardness | H358/30 | ISO2039-1 | 95.0 | Mpa |
optical performance | Test Condition | Test Method | Test Result | Unit |
---|
Haze | 2540µm | ASTMD1003 | <0.50 | % |
Refractive index of light | | ISO489 | 1.586 | |
2540µm | | ASTMD1003 | >90.0 | % |
2540µm,420nm | | 内部方法 | >88.0 | % |
5000µm | | 内部方法 | >89.0 | % |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 0.800mm,TestingbySABIC | UL94 | V-2 | |
Glow Wire Flammability Index | 1.00mm | IEC60695-2-12 | 850 | °C |
Oxygen Index | | ISO4589-2 | 25 | % |
Glow Wire Ignition Temperature | 1.00mm | IEC60695-2-13 | >875 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.