PC LUX2614-WH8E508X SABIC INNOVATIVE NANSHA

Unit Price:
$4284 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Flame retardant UV resistance
Application Areas:UV resistance Flame retardant
Color:--
Grade:Light diffusion level

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Moisture Absorption	24 hr	ASTM D570	0.15	%
	Moisture Absorption	Equilibrium, 23°C	ASTM D570	0.35	%
	Moisture Absorption	Moisture Absorption	Equilibrium, 100°C	ASTM D570	0.58	%
Melt Mass-Flow Rate	300°C/1.2 kg	ASTM D1238	7.0	g/10 min
Melt Volume flow Rate	300°C/1.2 kg	ISO 1133	7.00	cm3/10min
Specific Volume		ASTM D792	0.830	cm³/g
Outdoor Suitability		UL 746C	f2
Modeling Shrinkage - Flow	3.20 mm	内部方法	0.50 到 0.70	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Stress	-- 4, 5	ISO 178	94.0	Mpa
Flexural Stress	Flexural Stress	Yield, 50.0 mm Span 3	ASTM D790	93.0	Mpa
Taber Abrasion Resistance	1000 Cycles, 1000 g, CS-17 Wheel	ASTM D1044	10.0	mg
Tensile Strength	Yield 2	ASTM D638	62.0	Mpa
	Tensile Strength	Yield	ISO 527-2/50	63.0	Mpa
		Tensile Strength	Break 2	ASTM D638	65.0	Mpa
		Tensile Strength	Tensile Strength	Break	ISO 527-2/50	63.0	Mpa
Tensile Modulus		ISO 527-2/1	2300	Mpa
Tensile Elongation	Yield 2	ASTM D638	7.0	%
	Tensile Elongation	Yield	ISO 527-2/50	6.0	%
	Tensile Elongation	Tensile Elongation	Break 2	ASTM D638	110	%
Flexural Modulus	50.0 mm Span 3	ASTM D790	2340	Mpa
Flexural Modulus	Flexural Modulus	-- 4	ISO 178	2300	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Vicat Softening Temperature	--	ASTM D15257	154	°C
Vicat Softening Temperature	Vicat Softening Temperature	--	ISO 306/B120	145	°C
Specific Heat		ASTM C351	1260	J/kg/°C
Thermal Conductivity		ASTM C177	0.29	W/m/K
RTI		UL 746	80.0	°C
RTI Imp		UL 746	80.0	°C
RTI Elec		UL 746	80.0	°C
Deflection Temperature Under Load?	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	137	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	132	°C
Ball PressureTest	123 to 127°C	IEC 60695-10-2	通过
Coefficient of Linear Thermal Expansion (Flow)	-40 to 95°C	ASTM E831	6.8E-5	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Comparative Tracking Index		UL 746	PLC 3
Hot-wire Ignition		UL 746	PLC 3
Dielectric Strength	3.20 mm, in Air	ASTM D149	15	KV/mm
High Amp Arc Ignition		UL 746	PLC 1
Dissipation Factor?	50 Hz	ASTM D150	9.0E-4
	Dissipation Factor?	60 Hz	ASTM D150	9.0E-4
	Dissipation Factor?	Dissipation Factor?	1 MHz	ASTM D150	0.010
Dielectric Constant	60 Hz	ASTM D150	3.17
	Dielectric Constant	50 kHz	ASTM D150	3.17
	Dielectric Constant	Dielectric Constant	1 MHz	ASTM D150	2.96
Volume Resistivity		ASTM D257	> 1.0E+17	ohms·cm

Injection	Test Result	Unit
Drying Time	3.0 到 4.0	hr
Suggested Shot Size	40 到 60	%
Rear Temperature	290 到 310	°C
Middle Temperature	300 到 320	°C
Front Temperature	310 到 330	°C
Nozzle Temperature	305 到 325	°C
Back Pressure	0.300 到 0.700	Mpa
Screw Speed	40 到 70	rpm
Vent Depth	0.025 到 0.076	mm
Drying Temperature	120	°C
Suggested Max Moisture	0.020	%
Processing (Melt) Temp	310 到 330	°C
Mold Temperature	80 到 115	°C

Impact Properties	Test Condition	Test Method	Test Result	Unit
Gardner Impact	23°C	ASTM D3029	169	J
Unnotched Izod Impact Strength	23°C	ASTM D4812	3200	J/m
Tensile Impact Strength		ASTM D1822	546	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	M-Scale	ASTM D785	70
Rockwell Hardness	Rockwell Hardness	R-Scale	ASTM D785	118

optical performance	Test Condition	Test Method	Test Result	Unit
Refractive index of light		ASTM D542	1.586

Flammability	Test Condition	Test Method	Test Result	Unit
Glow Wire Flammability Index	0.75 mm	IEC 60695-2-12	750	°C
Glow Wire Flammability Index	Glow Wire Flammability Index	1.5 mm	IEC 60695-2-12	850	°C
Glow Wire Ignition Temperature	0.75 mm 9	IEC 60695-2-13	875	°C
Glow Wire Ignition Temperature	Glow Wire Ignition Temperature	1.5 mm	IEC 60695-2-13	850	°C
Flame Rating	0.8 to 1.7 mm	UL 94	V-2

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.