PC SABIC® 2200R SABIC INNOVATIVE SAUDI
88
- Unit Price:
- $1863 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 219MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High impact resistance High temperature resistan transparent High mobility
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Moisture Absorption | Saturation, 23°C | ISO 62 | 0.35 | % |
| Equilibrium, 23°C | ASTM D570 | 0.35 | % | |
| Melt Mass-Flow Rate | 300°C/1.2 kg | ASTM D1238 | 22 | g/10 min |
| Melt Volume flow Rate | 300°C/1.2 kg | ISO 1133 | 21.0 | cm3/10min |
| Modeling Shrinkage - Flow | -- 2 | 内部方法 | 0.50 到 0.70 | % |
| 3.20 mm | 内部方法 | 0.50 到 0.70 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Strength | Yield 4 | ASTM D638 | 63.0 | Mpa |
| Yield | ISO 527-2/50 | 63.0 | Mpa | |
| Flexural Stress | -- 6, 7 | ISO 178 | 90.0 | Mpa |
| Yield, 50.0 mm Span 5 | ASTM D790 | 90.0 | Mpa | |
| Tensile Modulus | -- 3 | ASTM D638 | 2350 | Mpa |
| -- | ISO 527-2/1 | 2350 | Mpa | |
| Tensile Elongation | Yield 4 | ASTM D638 | 6.0 | % |
| Yield | ISO 527-2/50 | 6.0 | % | |
| Break 4 | ASTM D638 | > 70 | % | |
| Break | ISO 527-2/50 | > 70 | % | |
| Flexural Modulus | 50.0 mm Span 5 | ASTM D790 | 2300 | Mpa |
| -- 6 | ISO 178 | 2300 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat Softening Temperature | ISO 306/B50, ASTM D152510 | 140 | °C | |
| Deflection Temperature Under Load? | 0.45 MPa, Unannealed, 3.20 mm | ASTM D648 | 133 | °C |
| 0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span 9 | ISO 75-2/Bf | 133 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 122 | °C | |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 9 | ISO 75-2/Af | 122 | °C | |
| Ball PressureTest | 123 to 127°C | IEC 60695-10-2 | 通过 | |
| Thermal Conductivity | ASTM C177, ISO 8302 | 0.20 | W/m/K | |
| Coefficient of Linear Thermal Expansion (Flow) | -40 to 95°C | ASTM E831 | 7.0E-5 | cm/cm/°C |
| 23 to 80°C | ISO 11359-2 | 7.0E-5 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric Strength | 1.60 mm | ASTM D149, IEC 60243-1 | 27 | KV/mm |
| Dissipation Factor? | 60 Hz | ASTM D150, IEC 60250 | 1.0E-3 | |
| 1 MHz | ASTM D150, IEC 60250 | 0.010 | ||
| Dielectric Constant | 60 Hz | ASTM D150, IEC 60250 | 3.00 | |
| 1 MHz | ASTM D150, IEC 60250 | 3.00 | ||
| Volume Resistivity | ASTM D257, IEC 60093 | > 1.0E+15 | ohms·cm |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Drying Temperature | 120 | °C | ||
| Suggested Max Moisture | 0.020 | % | ||
| Processing (Melt) Temp | 280 到 300 | °C | ||
| Mold Temperature | 80 到 100 | °C | ||
| Drying Time | 2.0 到 4.0 | hr | ||
| Rear Temperature | 260 到 280 | °C | ||
| Middle Temperature | 270 到 290 | °C | ||
| Front Temperature | 280 到 300 | °C | ||
| Nozzle Temperature | 270 到 290 | °C | ||
| Hopper Temperature | 60 到 80 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Instrumented Dart Impact | 23°C, Energy at Peak | ASTM D3763 | 55.0 | J |
| Unnotched Izod Impact Strength | 23°C | ASTM D4812, ISO 180/1U | 无断裂 | |
| -30°C 8 | ISO 180/1U | 无断裂 |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell Hardness | R-Scale | ASTM D785 | 120 | |
| R -Sale | ISO 2039-2 | 120 |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Refractive index of light | ISO 179/leA | 1.586 | ||
| Transmittance | 2540 µm | ASTM D1003 | 88.0 到 90.0 | % |
| Haze | 2540 µm | ASTM D1003 | < 0.80 | % |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flame Rating | 1.5 mm | UL 94 | V-2 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.