PC Makrolon® RX2530 451118 COVESTRO THAILAND
52
- Unit Price:
- $6737 USD/MT
- Packaging Specification:
- 25KG/PKG
- Supply Quantity:
- 49MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | TD | ISO2577 | 0.60to0.80 | % |
| MD | ISO2577 | 0.60to0.80 | % | |
| TD:2.00mm3 | ISO294-4 | 0.65 | % | |
| MD:2.00mm3 | ISO294-4 | 0.60 | % | |
| Moisture Absorption | Saturation,23°C | ISO62 | 0.30 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.12 | % | |
| Apparent Density | ISO60 | 0.66 | g/cm³ | |
| Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 15.0 | cm3/10min |
| Melt Mass-Flow Rate | 300°C/1.2kg | ISO1133 | 16 | g/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Nominal Tensile Strain at Break | 23°C | ISO527-2/50 | >50 | % |
| Flexural Stress | 3.5%Strain,23°C | ISO178 | 74.0 | Mpa |
| 23°C | ISO178 | 100 | Mpa | |
| Flexural Modulus | 23°C | ISO178 | 2400 | Mpa |
| Tensile Stress | Yield,23°C | ISO527-2/50 | 67.0 | Mpa |
| Break,23°C | ISO527-2/50 | 75.0 | Mpa | |
| Tensile Strain | Yield,23°C | ISO527-2/50 | 6.1 | % |
| Break,23°C | ISO527-2/50 | 130 | % | |
| Tensile Modulus | 23°C | ISO527-2/1 | 2400 | Mpa |
| Flexural Strain | 23°C | ISO178 | 7.0 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Glass Transition Temperature | ISO11357-2 | 142 | °C | |
| Thermal Conductivity | 23°C | ISO8302 | 0.20 | W/m/K |
| Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 134 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 122 | °C | |
| Vicat Softening Temperature | -- | ISO306/B50 | 141 | °C |
| -- | ISO306/B120 | 142 | °C | |
| Linear thermal expansion coefficient | MD：23to55°C | ISO11359-2 | 6.5E-05 | cm/cm/°C |
| TD：23to55°C | ISO11359-2 | 6.5E-05 | cm/cm/°C | |
| Ball PressureTest | 132°C | IEC60695-10-2 | Pass |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface Resistivity | IEC60093 | 1E+16 | ohms | |
| Volume Resistivity | 23°C | IEC60093 | 1E+16 | ohms·cm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | -60°C | ISO179/1eU | NoBreak | |
| -30°C | ISO179/1eU | NoBreak | ||
| 23°C | ISO179/1eU | NoBreak | ||
| Multi-Axial Instrumented Impact Energy | -30°C | ISO6603-2 | 70.0 | J |
| 23°C | ISO6603-2 | 60.0 | J | |
| Notched Izod Impact Strength | -30°C,Complete Break | ISO7391 | 12 | kJ/m² |
| 23°C,Partial Break | ISO7391 | 65 | kJ/m² | |
| Multi-Axial Instrumented Impact Peak Force | -30°C | ISO6603-2 | 6200 | N |
| 23°C | ISO6603-2 | 5300 | N | |
| Charpy Notched Impact Strength | -30°C,Complete Break | ISO7391 | 14 | kJ/m² |
| 23°C,Partial Break | ISO7391 | 70 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball Indentation Hardness | ISO2039-1 | 118 | Mpa |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| FlashIgnition | ASTMD1929 | 480 | °C | |
| Oxygen Index | ISO4589-2 | 27 | % | |
| SelfIgnition | ASTMD1929 | 550 | °C |
| Supplementary information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| ISO Shortname | ISO7391-PC,M,(,,)-18-9 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.