PC LEXAN™ EXL9330 BK1A233 SABIC INNOVATIVE US
73
- Unit Price:
- $4686 USD/MT
- Packaging Specification:
- 25KG/PKG
- Supply Quantity:
- 307.6MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Modeling Shrinkage | Flow : 3.20 mm | 内部方法 | 0.40 到 0.80 | % |
Across Flow : 3.20 mm | 内部方法 | 0.40 到 0.80 | % | |
Moisture Absorption | Saturation, 23°C | ISO 62 | 0.35 | % |
Equilibrium, 23°C, 50% RH | ISO 62 | 0.15 | % | |
Outdoor Suitability | UL 746C | f1 | ||
UL 746C | f1 | |||
Melt Mass-Flow Rate | 300°C/1.2 kg | ASTM D1238 | 10 | g/10 min |
Melt Volume flow Rate | 300°C/1.2 kg | ISO 1133 | 9.00 | cm3/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Flexural Stress | -- 5, 6 | ISO 178 | 85.0 | Mpa |
Yield, 50.0 mm Span 4 | ASTM D790 | 88.0 | Mpa | |
Tensile Strength | Yield 3 | ASTM D638 | 58.0 | Mpa |
Yield | ISO 527-2/50 | 55.0 | Mpa | |
Break 3 | ASTM D638 | 61.0 | Mpa | |
Break | ISO 527-2/50 | 60.0 | Mpa | |
Tensile Modulus | -- 2 | ASTM D638 | 2100 | Mpa |
-- | ISO 527-2/1 | 2100 | Mpa | |
Tensile Elongation | Yield 3 | ASTM D638 | 6.0 | % |
Yield | ISO 527-2/50 | 6.0 | % | |
Break 3 | ASTM D638 | 130 | % | |
Break | ISO 527-2/50 | 130 | % | |
Flexural Modulus | 50.0 mm Span 4 | ASTM D790 | 2060 | Mpa |
-- 5 | ISO 178 | 2200 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Vicat Softening Temperature | -- | ASTM D152512, ISO 306/B12012 | 142 | °C |
-- | ISO 306/B50 | 140 | °C | |
Linear thermal expansion coefficient | Flow : -40 to 40°C | ASTM E831 | 6.7E-5 | cm/cm/°C |
Flow : 23 to 80°C | ISO 11359-2 | 7.2E-5 | cm/cm/°C | |
Across Flow : -40 to 40°C | ASTM E831 | 6.7E-5 | cm/cm/°C | |
Across Flow : 23 to 80°C | ISO 11359-2 | 7.7E-5 | cm/cm/°C | |
RTI | UL 746 | 125 | °C | |
UL 746 | 125 | °C | ||
RTI Imp | UL 746 | 115 | °C | |
UL 746 | 115 | °C | ||
RTI Elec | UL 746 | 125 | °C | |
UL 746 | 125 | °C | ||
Deflection Temperature Under Load? | 0.45 MPa, Unannealed, 3.20 mm | ASTM D648 | 134 | °C |
0.45 MPa, Unannealed, 4.00 mm, 100 mm Span 11 | ISO 75-2/Be | 135 | °C | |
1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 120 | °C | |
1.8 MPa, Unannealed, 6.40 mm | ASTM D648 | 124 | °C | |
1.8 MPa, Unannealed, 4.00 mm, 100 mm Span 11 | ISO 75-2/Ae | 124 | °C | |
Ball PressureTest | 123 to 127°C | IEC 60695-10-2 | 通过 |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Dissipation Factor? | 50 Hz | ASTM D150 | 2.4E-3 | |
60 Hz | ASTM D150 | 2.4E-3 | ||
1 MHz | ASTM D150, IEC 60250 | 8.5E-3 | ||
50 Hz | IEC 60250 | 1.0E-3 | ||
60 Hz | IEC 60250 | 1.0E-3 | ||
Surface Resistivity | IEC 60093 | > 1.0E+15 | ohms | |
IEC 60093 | > 1.0E+15 | ohms | ||
Dielectric Constant | 60 Hz | ASTM D150 | 2.95 | |
50 kHz | ASTM D150 | 2.95 | ||
1 MHz | ASTM D150 | 2.90 | ||
50 Hz | IEC 60250 | 2.60 | ||
60 Hz | IEC 60250 | 2.60 | ||
1 MHz | IEC 60250 | 2.70 | ||
Volume Resistivity | IEC 60093 | > 1.0E+15 | ohms·cm | |
IEC 60093 | > 1.0E+15 | ohms·cm | ||
Dielectric Strength | 3.20 mm, in Oil | ASTM D149 | 17 | KV/mm |
3.20 mm, in Oil | IEC 60243-1 | 16 | KV/mm | |
Comparative Tracking Index | IEC 60112 | 225 | V | |
IEC 60112 | 225 | V | ||
Comparative Tracking Index | UL 746 | PLC 3 | ||
UL 746 | PLC 3 | |||
Hot-wire Ignition | UL 746 | PLC 1 | ||
UL 746 | PLC 1 | |||
High Amp Arc Ignition | UL 746 | PLC 0 | ||
UL 746 | PLC 0 |
Injection | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Drying Time | 3.0 到 4.0 | hr | ||
3.0 到 4.0 | hr | |||
Suggested Shot Size | 40 到 60 | % | ||
40 到 60 | % | |||
Rear Temperature | 215 到 295 | °C | ||
215 到 295 | °C | |||
Middle Temperature | 280 到 305 | °C | ||
280 到 305 | °C | |||
Front Temperature | 295 到 315 | °C | ||
295 到 315 | °C | |||
Nozzle Temperature | 290 到 310 | °C | ||
290 到 310 | °C | |||
Back Pressure | 0.300 到 0.700 | Mpa | ||
0.300 到 0.700 | Mpa | |||
Screw Speed | 40 到 70 | rpm | ||
40 到 70 | rpm | |||
Vent Depth | 0.025 到 0.076 | mm | ||
0.025 到 0.076 | mm | |||
Drying Temperature | 120 | °C | ||
120 | °C | |||
Suggested Max Moisture | 0.020 | % | ||
0.020 | % | |||
Processing (Melt) Temp | 295 到 315 | °C | ||
295 到 315 | °C | |||
Mold Temperature | 70 到 95 | °C | ||
70 到 95 | °C |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Unnotched Izod Impact Strength | -30°C | ISO 180/1U | 无断裂 | |
23°C | ISO 180/1U | 无断裂 | ||
Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 60 | kJ/m² |
23°C | ISO 179/1eA | 75 | kJ/m² | |
Charpy Unnotched Impact Strength | -30°C | ISO 179/1eU | 无断裂 | |
23°C | ISO 179/1eU | 无断裂 | ||
Instrumented Dart Impact | 23°C, Total Energy | ASTM D3763 | 52.0 | J |
hardness | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Ball Indentation Hardness | H 358/30 | ISO 2039-1 | 90.0 | Mpa |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Glow Wire Flammability Index | 1.0 mm | IEC 60695-2-12 | 960 | °C |
Oxygen Index | ISO 4589-2 | 35 | % | |
ISO 4589-2 | 35 | % | ||
Glow Wire Ignition Temperature | 1.0 mm | IEC 60695-2-13 | 825 | °C |
Flame Rating | 1.5 mm | UL 94 | V-0 | |
3.0 mm | UL 94 | 5VA |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.