PC Makrolon® RX1805 451118 COVESTRO GERMANY
161
- Unit Price:
- $7339 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 71.8MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:transparent
- Application Areas:Medical Supplies
- Color:--
- Grade:Special level
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | TD:2.00mm3 | ISO294-4 | 0.70 | % |
| MD:2.00mm3 | ISO294-4 | 0.70 | % | |
| TD | ISO2577 | 0.60to0.80 | % | |
| MD | ISO2577 | 0.60to0.80 | % | |
| Moisture Absorption | Saturation,23°C | ISO62 | 0.30 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.12 | % | |
| Melt Mass-Flow Rate | 300°C/1.2kg | ISO1133 | 6.5 | g/10min |
| Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 6.00 | cm3/10min |
| Density / Specific Gravity | 23°C | ISO1183 | 1.20 | g/cm³ |
| Apparent Density | ISO60 | 0.66 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural Strain | 23°C | ISO178 | 7.1 | % |
| Flexural Stress | 3.5%Strain,23°C | ISO178 | 73.0 | Mpa |
| 23°C | ISO178 | 98.0 | Mpa | |
| Flexural Modulus | 23°C | ISO178 | 2400 | Mpa |
| Nominal Tensile Strain at Break | 23°C | ISO527-2/50 | >50 | % |
| Tensile Modulus | 23°C | ISO527-2/1 | 2400 | Mpa |
| Tensile Stress | Yield,23°C | ISO527-2/50 | 67.0 | Mpa |
| Break,23°C | ISO527-2/50 | 75.0 | Mpa | |
| Tensile Strain | Yield,23°C | ISO527-2/50 | 6.3 | % |
| Break,23°C | ISO527-2/50 | 130 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 138 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 126 | °C | |
| Vicat Softening Temperature | -- | ISO306/B50 | 144 | °C |
| -- | ISO306/B120 | 145 | °C | |
| Linear thermal expansion coefficient | MD：23to55°C | ISO11359-2 | 6.5E-05 | cm/cm/°C |
| TD：23to55°C | ISO11359-2 | 6.5E-05 | cm/cm/°C | |
| Ball PressureTest | 135°C | IEC60695-10-2 | Pass | |
| Glass Transition Temperature | ISO11357-2 | 145 | °C | |
| Thermal Conductivity | 23°C | ISO8302 | 0.20 | W/m/K |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Multi-Axial Instrumented Impact Energy | -30°C | ISO6603-2 | 70.0 | J |
| 23°C | ISO6603-2 | 65.0 | J | |
| Notched Izod Impact Strength | -30°C,Complete Break | ISO7391 | 15 | kJ/m² |
| 23°C,Partial Break | ISO7391 | 70 | kJ/m² | |
| Multi-Axial Instrumented Impact Peak Force | -30°C | ISO6603-2 | 6600 | N |
| 23°C | ISO6603-2 | 5700 | N | |
| Charpy Unnotched Impact Strength | -60°C | ISO179/1eU | NoBreak | |
| -30°C | ISO179/1eU | NoBreak | ||
| 23°C | ISO179/1eU | NoBreak | ||
| Charpy Notched Impact Strength | -30°C,Complete Break | ISO7391 | 16 | kJ/m² |
| 23°C,Partial Break | ISO7391 | 80 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball Indentation Hardness | ISO2039-1 | 114 | Mpa |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| FlashIgnition | ASTMD1929 | 480 | °C | |
| Oxygen Index | ISO4589-2 | 27 | % | |
| SelfIgnition | ASTMD1929 | 550 | °C |
| Supplementary information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| ISO Shortname | ISO7391-PC,M,(,,)-09-9 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.