PC Makrolon® LED-2245 COVESTRO GERMANY
185
- Unit Price:
- $3997 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 110.8MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High temperature resistan High mobility Flame retardant Antichemical transparent
- Application Areas:Electrical field Electronic field Optical applications lens Automotive sector Lighting fixtures Lighting applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | Saturation,23°C | ISO62 | 0.30 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.12 | % | |
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 34.0 | cm3/10min |
| Density/specific gravity | 23°C | ISO1183 | 1.19 | g/cm³ |
| Apparent density 2 | ISO60 | 0.66 | g/cm³ | |
| Shrinkage rate 3 | TD:2.00mm | ISO294-4 | 0.70 | % |
| MD:2.00mm | ISO294-4 | 0.65 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Nominal tensile fracture strain | 23°C | ISO527-2/50 | >50 | % |
| Bending strain 5 | 23°C | ISO178 | 7.1 | % |
| Bending stress 4 | 3.5%Strain,23°C | ISO178 | 73.0 | Mpa |
| 23°C | ISO178 | 97.0 | Mpa | |
| Bending modulus 4 | 23°C | ISO178 | 2350 | Mpa |
| Tensile stress | Yield,23°C | ISO527-2/50 | 63.0 | Mpa |
| Break,23°C | ISO527-2/50 | 60.0 | Mpa | |
| Tensile strain | Yield,23°C | ISO527-2/50 | 6.0 | % |
| Break,23°C | ISO527-2/50 | 130 | % | |
| Tensile modulus | 23°C | ISO527-2/1 | 2350 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 125 | °C |
| 0.45MPa,Unannealed | ISO75-2/B | 138 | °C | |
| RTIElec | 1.5mm | UL746 | 125 | °C |
| Evolution Calendar intelligent importer | 1.5mm | UL746 | 115 | °C |
| RTIStr | 1.5mm | UL746 | 125 | °C |
| Vicat softening temperature | -- | ISO306/B50 | 145 | °C |
| -- | ISO306/B120 | 146 | °C | |
| BallPressure Test | 136°C | IEC60695-10-2 | Pass | |
| Linear coefficient of thermal expansion | MD：23to55°C | ISO11359-2 | 6.5E-05 | cm/cm/°C |
| TD：23to55°C | ISO11359-2 | 6.5E-05 | cm/cm/°C | |
| Glass transition temperature 8 | ISO11357-2 | 145 | °C | |
| Thermal conductivity coefficient 9 | 23°C | ISO8302 | 0.20 | W/m/K |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric strength | 23°C,1.00mm | IEC60243-1 | 34 | KV/mm |
| Relative permittivity | 23°C,100Hz | IEC60250 | 3.10 | |
| 23°C,1MHz | IEC60250 | 3.00 | ||
| Leakage Trace Index | SolutionA | IEC60112 | 250 | V |
| SolutionB | IEC60112 | 125 | V | |
| Dissipation factor | 23°C,100Hz | IEC60250 | 5E-04 | |
| 23°C,1MHz | IEC60250 | 9.5E-03 | ||
| Surface resistivity | IEC60093 | 1E+16 | ohms | |
| Volume resistivity | 23°C | IEC60093 | 1E+16 | ohms·cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -60°C | ISO179/1eU | NoBreak | |
| -30°C | ISO179/1eU | NoBreak | ||
| 23°C | ISO179/1eU | NoBreak | ||
| Impact strength of simply supported beam gap 6 | -30°C,Complete Break | ISO7391 | 12 | kJ/m² |
| 23°C,Partial Break | ISO7391 | 60 | kJ/m² | |
| Multi axis Instrumented Impact Energy | -30°C | ISO6603-2 | 60.0 | J |
| 23°C | ISO6603-2 | 55.0 | J | |
| Suspended wall beam gap impact strength 7 | -30°C,Complete Break | ISO7391 | 12 | kJ/m² |
| 23°C,Partial Break | ISO7391 | 55 | kJ/m² | |
| Multi axis Instrumented Peak Impact Force | -30°C | ISO6603-2 | 5900 | N |
| 23°C | ISO6603-2 | 4900 | N |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball pressure hardness | ISO2039-1 | 115 | Mpa |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Haze | 3000µm | ISO14782 | <0.50 | % |
| transmissivity | 1000µm | ISO13468-2 | 90.0 | % |
| 2000µm | ISO13468-2 | 90.0 | % | |
| 3000µm | ISO13468-2 | >89.0 | % | |
| 4000µm | ISO13468-2 | >89.0 | % | |
| Refractive Index11 | ISO489 | 1.584 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Burning rate - US-FMVSS | >1.00mm | ISO3795 | passed | |
| FlashIgnitionTemperature | ASTMD1929 | 480 | °C | |
| Extreme Oxygen Index 10 | ISO4589-2 | 28 | % | |
| SelfIgnition | ASTMD1929 | 550 | °C | |
| UL flame retardant rating | 2.9mm,CL | UL94 | HB | |
| 0.75mm,CL | UL94 | V-2 | ||
| Burning wire flammability index | 1.0mm | IEC60695-2-12 | 850 | °C |
| 1.5mm | IEC60695-2-12 | 875 | °C | |
| 3.0mm | IEC60695-2-12 | 930 | °C | |
| Hot filament ignition temperature | 0.75mm | IEC60695-2-13 | 875 | °C |
| 1.5mm | IEC60695-2-13 | 875 | °C | |
| 3.0mm | IEC60695-2-13 | 900 | °C |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| ISO Shortcut | ISO7391-PC,MRT,(,,)-24-9 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.