PC Makrolon® APEC 2097 COVESTRO GERMANY

159

Unit Price:
$12492 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
46MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:UV curing Good demolding performanc High temperature resistan High mobility
Application Areas:Nursing supplies Automotive sector Medical supplies Lighting fixtures
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Moisture Absorption	Saturation, 23°C	ISO 62	0.30	%
Moisture Absorption	Moisture Absorption	Equilibrium, 23°C, 50% RH	ISO 62	0.12	%
Melt Mass-Flow Rate	330°C/2.16 kg	ISO 1133	8.0	g/10 min
Melt Volume flow Rate	330°C/2.16 kg	ISO 1133	8.00	cm3/10min
Density	23°C	ISO 1183	1.13	g/cm³
Modeling Shrinkage	Across Flow : 2.00 mm	ISO 294-4	0.90	%
Modeling Shrinkage	Modeling Shrinkage	流量 : 2.00 mm	ISO 294-4	0.90	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Nominal Tensile Strain at Break	23°C	ISO 527-2/50	> 50	%
Tensile Stress	Yield, 23°C	ISO 527-2/50	76.0	Mpa
Tensile Strain	Yield, 23°C	ISO 527-2/50	6.9	%
Tensile Modulus	23°C	ISO 527-2/1	2450	Mpa
Flexural Modulus	23°C	ISO 178	2450	Mpa
Flexural Stress	23°C	ISO 178	110	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Linear thermal expansion coefficient	Flow : 23 to 55°C	ISO 11359-2	6.5E-5	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	Across Flow : 23 to 55°C	ISO 11359-2	6.5E-5	cm/cm/°C
Deflection Temperature Under Load?	0.45 MPa, Unannealed	ISO 75-2/B	191	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed	ISO 75-2/A	172	°C
RTI		UL 746	150	°C
RTI Imp		UL 746	130	°C
RTI Elec		UL 746	150	°C
Vicat Softening Temperature		ISO 306/B120	202	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface Resistivity		IEC 60093	1.0E+16	ohms
Volume Resistivity	23°C	IEC 60093	1.0E+17	ohms·cm
Dissipation Factor?	23°C, 100 Hz	IEC 60250	1.0E-3
Dissipation Factor?	Dissipation Factor?	23°C, 1 MHz	IEC 60250	9.0E-3
Dielectric Strength	23°C, 1.00 mm	IEC 60243-1	35	KV/mm
Relative Permittivity	23°C, 100 Hz	IEC 60250	2.90
Relative Permittivity	Relative Permittivity	23°C, 1 MHz	IEC 60250	2.80
Comparative Tracking Index	Solution A	IEC 60112	600	V
Comparative Tracking Index	Comparative Tracking Index	Solution B	IEC 60112	100	V

Injection	Test Result	Unit
Suggested Max Moisture	< 0.020	%
Processing (Melt) Temp	330 到 340	°C
Mold Temperature	110 到 150	°C
Suggested Shot Size	30 到 70	%
Rear Temperature	315 到 325	°C
Middle Temperature	320 到 330	°C
Front Temperature	325 到 335	°C
Nozzle Temperature	315 到 340	°C
Back Pressure	10.0 到 20.0	Mpa
Vent Depth	0.025 到 0.050	mm
Drying Temperature ()	130	°C
Dry Air Dryer	2.0 到 4.0	hr

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Unnotched Impact Strength	-30°C	ISO 179/1eU	无断裂
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO 179/1eU	无断裂

hardness	Test Condition	Test Method	Test Result	Unit
Ball Indentation Hardness		ISO 2039-1	130	Mpa

optical performance	Test Condition	Test Method	Test Result	Unit
Electrolytical Corrosion	23°C	IEC 60426	A1
Transmittance	1000 µm	ISO 13468-2	89.0	%
Index of Refraction		ISO 489	1.566

Flammability	Test Condition	Test Method	Test Result	Unit
Glow Wire Flammability Index		IEC 60695-2-12	800	°C
Flame Rating	1.5 mm	UL 94	HB
Oxygen Index		ISO 4589-2	25	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.