PC LEXAN™ HPS1R-1124 SABIC INNOVATIVE US
90
- Unit Price:
- $10269 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility
- Application Areas:medicine medical care
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.50to0.70 | % |
| Moisture Absorption | 24hr | ASTMD570 | 0.15 | % |
| Equilibrium,23°C | ASTMD570 | 0.35 | % | |
| Equilibrium,100°C | ASTMD570 | 0.58 | % | |
| Melt Mass-Flow Rate | 300°C/1.2kg | ASTMD1238 | 25 | g/10min |
| Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 23.0 | cm3/10min |
| Specific Volume | ASTMD792 | 0.835 | cm³/g |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural Modulus | ISO178 | 2300 | Mpa | |
| Flexural Strength | ISO178 | 90.0 | Mpa | |
| Tensile Modulus | ASTMD638 | 2380 | Mpa | |
| Tensile Strength | Yield | ASTMD638 | 62.1 | Mpa |
| Break | ASTMD638 | 65.5 | Mpa | |
| Flexural Modulus | 50.0mmSpan | ASTMD790 | 2310 | Mpa |
| Flexural Strength | Yield,50.0mmSpan | ASTMD790 | 93.1 | Mpa |
| Tensile Elongation | Break | ASTMD638 | 120 | % |
| Tensile Elongation | Yield | ASTMD638 | 6.0 | % |
| Taber Abrasion Resistance | 1000Cycles,1000g,CS-17Wheel | ASTMD1044 | 10.0 | mg |
| Tensile Stress | Yield | ISO527-2/50 | 63.0 | Mpa |
| Break | ISO527-2/50 | 50.0 | Mpa | |
| Tensile Strain | Break | ISO527-2/50 | 70 | % |
| Yield | ISO527-2/50 | 6.0 | % | |
| Tensile Modulus | ISO527-2/1 | 2350 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45MPa,Unannealed,6.40mm | ASTMD648 | 138 | °C |
| 1.8MPa,Unannealed,6.40mm | ASTMD648 | 127 | °C | |
| Linear thermal expansion coefficient | MD：-40to95°C | ASTME831 | 6.8E-05 | cm/cm/°C |
| MD：23to80°C | ISO11359-2 | 7E-05 | cm/cm/°C | |
| Specific Heat | ASTMC351 | 1260 | J/kg/°C | |
| Thermal Conductivity | ASTMC177 | 0.19 | W/m/K | |
| ISO8302 | 0.20 | W/m/K | ||
| Vicat Softening Temperature | -- | ISO306/B50 | 139 | °C |
| -- | ISO306/B120 | 140 | °C | |
| Ball PressureTest | 125°C | IEC60695-10-2 | Pass | |
| Heat Deflection Temperature | 1.8MPa,Unannealed,100mmSpan | ISO75-2/Ae | 121 | °C |
| 0.45MPa,Unannealed,100mmSpan | ISO75-2/Be | 133 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric Strength | 3.20mm,inAir | ASTMD149 | 15 | KV/mm |
| 3.20mm,in Oil | IEC60243-1 | 17 | KV/mm | |
| Relative Permittivity | 50Hz | IEC60250 | 2.70 | |
| 60Hz | IEC60250 | 2.70 | ||
| 1MHz | IEC60250 | 2.70 | ||
| Surface Resistivity | IEC60093 | >1.0E+15 | ohms | |
| Dielectric Constant | 50Hz | ASTMD150 | 3.17 | |
| 60Hz | ASTMD150 | 3.17 | ||
| 1MHz | ASTMD150 | 2.96 | ||
| Volume Resistivity | ASTMD257 | >1.0E+17 | ohms·cm | |
| IEC60093 | >1.0E+15 | ohms·cm | ||
| Dissipation Factor? | 50Hz | ASTMD150 | 9E-04 | |
| 60Hz | ASTMD150 | 9E-04 | ||
| 1MHz | ASTMD150 | 0.010 | ||
| 50Hz | IEC60250 | 1E-03 | ||
| 60Hz | IEC60250 | 1E-03 | ||
| 1MHz | IEC60250 | 0.010 |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Gardner Impact | 23°C | ASTMD3029 | 169 | J |
| Tensile Impact Strength | ASTMD1822 | 378 | kJ/m² | |
| Unnotched Izod Impact Strength | -30°C | ISO180/1U | NoBreak | |
| 23°C | ISO180/1U | NoBreak | ||
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 10 | kJ/m² |
| 23°C | ISO179/1eA | 12 | kJ/m² | |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 12 | kJ/m² |
| -30°C | ISO180/1A | 10 | kJ/m² | |
| Instrumented Dart Impact | 23°C,EnergyatPeakLoad | ASTMD3763 | 54.2 | J |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell Hardness | M-Sale | ASTMD785 | 70 | |
| R-Sale | ASTMD785 | 118 | ||
| Ball Indentation Hardness | H358/30 | ISO2039-1 | 95.0 | Mpa |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Refractive index of light | ASTMD542 | 1.586 | ||
| Haze | 2540µm | ASTMD1003 | 1.0 | % |
| Transmittance | 2540µm | ASTMD1003 | 88.0 | % |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Oxygen Index | ISO4589-2 | 25 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.