PC LEXAN™ EXL4019-WH8D346 SABIC INNOVATIVE NANSHA
66
- Unit Price:
- $4918 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 18MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Middle flow Short molding cycle Good ductility
- Application Areas:Electronic and Electrical Electronic display
- Color:--
- Grade:Enhanced level
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Mass-Flow Rate | 300°C/1.2 kg | ASTM D1238 | 7.5 | g/10 min |
| Melt Volume flow Rate | 300°C/1.2 kg | ISO 1133 | 6.00 | cm3/10min |
| Modeling Shrinkage | Across Flow : 3.20 mm | 内部方法 | 0.20 到 0.60 | % |
| Flow : 3.20 mm | 内部方法 | 0.20 到 0.60 | % | |
| Moisture Absorption | Equilibrium, 23°C, 50% RH | ISO 62 | 0.40 | % |
| Saturation, 23°C | ISO 62 | 0.15 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Modulus | -- | ISO 527-2/1 | 3900 | Mpa |
| -- 2 | ASTM D638 | 3950 | Mpa | |
| Tensile Elongation | Break | ISO 527-2/5 | 8.7 | % |
| Break 3 | ASTM D638 | 14 | % | |
| Yield | ISO 527-2/5 | 4.3 | % | |
| Yield 3 | ASTM D638 | 4.3 | % | |
| Flexural Modulus | -- 5 | ISO 178 | 3450 | Mpa |
| 50.0 mm Span 4 | ASTM D790 | 3500 | Mpa | |
| Tensile Strength | Break | ISO 527-2/5 | 48.0 | Mpa |
| Break 3 | ASTM D638 | 45.0 | Mpa | |
| Yield | ISO 527-2/5 | 54.0 | Mpa | |
| Yield 3 | ASTM D638 | 55.0 | Mpa | |
| Flexural Stress | Yield, 50.0 mm Span 4 | ASTM D790 | 103 | Mpa |
| -- 5, 6 | ISO 178 | 98.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat Softening Temperature | ASTM D152510, ISO 306/B50, ISO 306/B120 | 146 | °C | |
| Deflection Temperature Under Load? | 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 137 | °C |
| 1.8 MPa, Unannealed, 4.00 mm, 100 mm Span 9 | ISO 75-2/Ae | 135 | °C | |
| Ball PressureTest | 73 to 77°C | IEC 60695-10-2 | 通过 | |
| Linear thermal expansion coefficient | Flow : -40 to 40°C | ASTM E831, ISO 11359-2 | 4.7E-5 | cm/cm/°C |
| Across Flow : -40 to 40°C | ASTM E831 | 7.0E-5 | cm/cm/°C | |
| Across Flow : -40°C | ISO 11359-2 | 7.0E-5 | cm/cm/°C |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Drying Time | 3.0 到 4.0 | hr | ||
| Suggested Shot Size | 40 到 60 | % | ||
| Rear Temperature | 290 到 310 | °C | ||
| Middle Temperature | 300 到 320 | °C | ||
| Front Temperature | 310 到 330 | °C | ||
| Nozzle Temperature | 305 到 325 | °C | ||
| Back Pressure | 0.300 到 0.700 | Mpa | ||
| Screw Speed | 40 到 70 | rpm | ||
| Vent Depth | 0.025 到 0.076 | mm | ||
| Drying Temperature | 120 | °C | ||
| Suggested Max Moisture | 0.020 | % | ||
| Processing (Melt) Temp | 310 到 330 | °C | ||
| Mold Temperature | 80 到 115 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 25 | kJ/m² |
| -30°C | ISO 179/1eA | 15 | kJ/m² | |
| Charpy Unnotched Impact Strength | 23°C | ISO 179/1eU | 无断裂 | |
| -30°C | ISO 179/1eU | 无断裂 | ||
| Unnotched Izod Impact Strength | -30°C | ISO 180/1U | 无断裂 | |
| 23°C | ISO 180/1U | 无断裂 | ||
| Instrumented Dart Impact | 23°C, Total Energy | ASTM D3763 | 40.0 | J |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flame Rating | 0.75 mm | UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.