Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | | ASTM D955 | 0.40-0.60 | % |
Moisture Absorption 23℃/24H | | ASTM D570/ISO 62 | 0.14 | % |
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | TD:4.00mm | 内部方法 | 0.40to0.60 | % |
Modeling Shrinkage | MD:4.00mm | 内部方法 | 0.10to0.30 | % |
Moisture Absorption | 23°C,24hr | ISO62 | 0.14 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | Break | ISO527-2/5 | 90.0 | Mpa |
Tensile Strain | Break | ISO527-2/5 | 3.0 | % |
Flexural Modulus | | ISO178 | 5700 | Mpa |
Flexural Stress | | ISO178 | 140 | Mpa |
Tensile Modulus | | ASTM D638/ISO 527 | 6200 | kg/cm²(MPa)[Lb/in²] |
Tensile Modulus | | ISO527-2/1 | 6200 | Mpa |
Tensile Strength | | ASTM D638/ISO 527 | 90.0 | kg/cm²(MPa)[Lb/in²] |
Flexural Modulus | | ASTM D790/ISO 178 | 5700 | kg/cm²(MPa)[Lb/in²] |
Flexural Strength | | ASTM D790/ISO 178 | 140 | kg/cm²(MPa)[Lb/in²] |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 149 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 146 | °C |
Deflection Temperature Under Load? | | ASTM D648/ISO 75 | 149 | ℃(℉) |
Vicat Softening Temperature | | ASTM D1525/ISO R306 | 151 | ℃(℉) |
Linear expansion coefficient | | ASTM D696/ISO 11359 | 0.000030 | mm/mm.℃ |
Linear thermal expansion coefficient | MD | ISO11359-2 | 3E-05 | cm/cm/°C |
Linear thermal expansion coefficient | TD | ISO11359-2 | 6E-05 | cm/cm/°C |
Vicat Softening Temperature | | ISO306/B50 | 151 | °C |
RTIElec | 1.5mm | UL746 | 130 | °C |
Evolution Calendar intelligent importer | 1.5mm | UL746 | 120 | °C |
RTIStr | 1.5mm | UL746 | 130 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dissipation Factor? | 100Hz | IEC60250 | 1E-03 | |
Dissipation Factor? | 1MHz | IEC60250 | 9E-03 | |
Comparative Tracking Index | | IEC60112 | 175 | V |
Dielectric Strength | | IEC60243-1 | 35 | KV/mm |
Surface Resistivity | | IEC60093 | >1.0E+15 | ohms |
Surface Resistivity | | ASTM D257/IEC 60093 | 1.0E+15 | Ω |
Dielectric Constant | | ASTM D150/IEC 60250 | 3.40 | |
Dielectric Constant | 100Hz | IEC60250 | 3.40 | |
Dielectric Constant | 1MHz | IEC60250 | 3.40 | |
Volume Resistivity | | IEC60093 | >1.0E+15 | ohms·cm |
Volume Resistivity | | ASTM D257/IEC 60093 | 1.0E+15 | Ω.cm |
Dielectric loss | | ASTM D150/IEC 60250 | 0.0010 | |
Dielectric loss | | ASTM D150/IEC 60250 | 0.0090 | |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | | ISO179 | 35 | kJ/m² |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 0.40mm | UL94 | V-2 | |
UL flame retardant rating | 0.75mm | UL94 | V-0 | |
UL flame retardant rating | 2.5mm | UL94 | 5VA | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.