PC INFINO® CF-3200HF Samsung Cheil South Korea

Unit Price:
$3435 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
30MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Glass fiber reinforced Flame retardant
Application Areas:Electronic and Electrical Phone
Color:--
Grade:--

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	Flow : 3.20 mm	ASTM D955	0.20 到 0.50	%
	Modeling Shrinkage	Across Flow : 3.20 mm	ASTM D955	0.20 到 0.50	%
		Modeling Shrinkage	Across Flow : 2.00 mm	ISO 294-4	0.20 到 0.50	%
		Modeling Shrinkage	Modeling Shrinkage	流量 : 2.00 mm	ISO 294-4	0.20 到 0.50	%
Moisture Absorption	Saturation, 23°C	ASTM D570, ISO 62	0.15	%
Melt Mass-Flow Rate	250°C/10.0 kg	ASTM D1238, ISO 1133	23	g/10 min
Density / Specific Gravity	本色	ASTM D792, ISO 1183	1.33	g/cm³

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Modulus	-- 3	ASTM D638	5300	Mpa
Tensile Modulus	Tensile Modulus	--	ISO 527-2/5	5700	Mpa
Tensile Elongation	Break 3	ASTM D638	4.3	%
Tensile Elongation	Tensile Elongation	Break	ISO 527-2/5	4.3	%
Flexural Modulus	-- 4	ASTM D790	5500	Mpa
Flexural Modulus	Flexural Modulus	-- 5	ISO 178	6000	Mpa
Flexural Strength	-- 4	ASTM D790	140	Mpa
Flexural Strength	Flexural Strength	-- 5	ISO 178	170	Mpa
Tensile Strength	Yield 3	ASTM D638	98.0	Mpa
	Tensile Strength	Yield	ISO 527-2/5	100	Mpa
		Tensile Strength	Break 3	ASTM D638	98.0	Mpa
		Tensile Strength	Tensile Strength	Break	ISO 527-2/5	200	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Vicat Softening Temperature		ISO 306/B50	148	°C
Deflection Temperature Under Load?	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	145	°C
	Deflection Temperature Under Load?	0.45 MPa, Unannealed, 4.00 mm	ISO 75-2/B	144	°C
		Deflection Temperature Under Load?	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	141	°C
		Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed, 4.00 mm	ISO 75-2/A	139	°C

Injection	Test Condition	Test Result	Unit
Rear Temperature		270	°C
Middle Temperature		280 到 290	°C
Front Temperature		300	°C
Nozzle Temperature		300	°C
Back Pressure		0.981 到 2.94	Mpa
Screw Speed		40 到 80	rpm
Injection Pressure		98.1	Mpa
Desiccant Dryer		2.0 到 4.0	hr
Desiccant Dryer	Desiccant Dryer		100	°C
vacuum dryer		100	°C
vacuum dryer	vacuum dryer		4.0 到 6.0	hr
Suggested Max Moisture		0.10	%
Mold Temperature		80 到 120	°C

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Notched Impact Strength	23°C	ISO 179/1eA	25	kJ/m²
Notched Izod Impact Strength	23°C, 3.18 mm	ASTM D256	190	J/m
	Notched Izod Impact Strength	23°C, 6.35 mm	ASTM D256	200	J/m
	Notched Izod Impact Strength	Notched Izod Impact Strength	23°C 6	ISO 180/1A	19	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	R-Scale	ASTM D785	116
Rockwell Hardness	Rockwell Hardness	R -Sale	ISO 2039-2	116

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating	0.8 mm	UL 94	V-2
Flame Rating	Flame Rating	3.2 mm	UL 94	V-1

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.