PC LEXAN™ EXL1414 WH9A320 SABIC INNOVATIVE NANSHA
140
- Unit Price:
- $5249 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 40MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Processability Moderate liquidity Ductility copolymer Good demolding performanc
- Application Areas:Electrical applications Home appliance components Fitness equipment
- Color:--
- Grade:Injection grade
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.40to0.80 | % |
| TD：3.20mm | 内部方法 | 0.40to0.80 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.35 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.15 | % | |
| Melt mass flow rate | 300°C/1.2kg | ASTMD1238 | 10 | g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 9.00 | cm3/10min |
| Density/specific gravity | ASTMD792 | 1.18 | g/cm³ | |
| ISO1183 | 1.19 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Elongation rate 3 | Yield | ASTMD638 | 6.0 | % |
| Bending strength 5,6 | ISO178 | 85.0 | Mpa | |
| Elongation rate 4 | Break | ASTMD638 | 98 | % |
| Bending modulus 5 | ISO178 | 2250 | Mpa | |
| Tensile modulus 2 | ASTMD638 | 2020 | Mpa | |
| Tensile strength 3 | Break | ASTMD638 | 50.3 | Mpa |
| Yield | ASTMD638 | 55.5 | Mpa | |
| Bending modulus 4 | 50.0mmSpan | ASTMD790 | 2230 | Mpa |
| Bending strength 4 | Yield,50.0mmSpan | ASTMD790 | 92.4 | Mpa |
| Tensile stress | Yield | ISO527-2/50 | 57.0 | Mpa |
| Break | ISO527-2/50 | 60.0 | Mpa | |
| Tensile strain | Yield | ISO527-2/50 | 6.0 | % |
| Break | ISO527-2/50 | 120 | % | |
| Tensile modulus | ISO527-2/1 | 2150 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 139 | °C |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 124 | °C | |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 7E-05 | cm/cm/°C |
| MD：23to80°C | ISO11359-2 | 7.2E-05 | cm/cm/°C | |
| TD：-40to40°C | ASTME831 | 7.5E-05 | cm/cm/°C | |
| TD：23to80°C | ISO11359-2 | 7.2E-05 | cm/cm/°C | |
| RTIElec | UL746 | 130 | °C | |
| Evolution Calendar intelligent importer | UL746 | 120 | °C | |
| RTIStr | UL746 | 125 | °C | |
| BallPressure Test | 125°C | IEC60695-10-2 | Pass | |
| Vicat softening temperature | -- | ISO306/B50 | 145 | °C |
| -- | ISO306/B120 | 146 | °C | |
| ASTMD152510 | 145 | °C | ||
| Hot deformation temperature 9 | 1.8MPa,Unannealed,100mmSpan | ISO75-2/Ae | 128 | °C |
| 0.45MPa,Unannealed,100mmSpan | ISO75-2/Be | 140 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dissipation factor | 100Hz | ASTMD150 | 1.2E-03 | |
| 1MHz | ASTMD150 | 9.3E-03 | ||
| Dielectric strength | 0.800mm,inOil | ASTMD149 | 16 | KV/mm |
| Surface resistivity | ASTMD257 | >1.0E+15 | ohms | |
| Dielectric constant | 100Hz | ASTMD150 | 2.68 | |
| 1MHz | ASTMD150 | 2.64 | ||
| Volume resistivity | ASTMD257 | >1.0E+15 | ohms·cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Unscented Izod Impact Strength 8 | -30°C | ISO180/1U | NoBreak | |
| 23°C | ISO180/1U | NoBreak | ||
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 70.0 | J |
| Impact strength of simply supported beam gap 7 | -30°C | ISO179/1eA | 65 | kJ/m² |
| 23°C | ISO179/1eA | 70 | kJ/m² | |
| The impact strength of a simply supported beam without a notch is 7 | -30°C | ISO179/1eU | NoBreak | |
| 23°C | ISO179/1eU | NoBreak | ||
| Suspended wall beam gap impact strength 8 | -30°C | ISO180/1A | 60 | kJ/m² |
| 23°C | ISO180/1A | 70 | kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ASTMD256 | 770 | J/m |
| 23°C | ASTMD256 | 870 | J/m |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | L-Sale | ASTMD785 | 89 | |
| R-Sale | ASTMD785 | 121 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot filament ignition temperature | 1.0mm | IEC60695-2-13 | 875 | °C |
| 3.0mm | IEC60695-2-13 | 875 | °C | |
| UL flame retardant rating | 0.40mm | UL94 | HB | |
| Burning wire flammability index | 0.8mm | IEC60695-2-12 | 850 | °C |
| 1.0mm | IEC60695-2-12 | 960 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.