PC LEXAN™ EXL1414T NA8A005T SABIC INNOVATIVE SHANGHAI
205
- Unit Price:
- $4621 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 40MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Low temperature resistanc transparent Processability Moderate liquidity Ductility copolymer
- Application Areas:Electrical field Electronic field Household appliances Household appliances Fitness equipment
- Color:--
- Grade:Injection grade
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt flow rate | 300°C/1.2 kg | ASTM D1238 | 10 | g/10 min |
| Molten Volume Flow Rate (MVR) | 300°C/1.2 kg | ISO 1133 | 9.00 | cm3/10min |
| Shrinkage rate | Flow : 3.20 mm | 内部方法 | 0.40 到 0.80 | % |
| Across Flow : 3.20 mm | 内部方法 | 0.40 到 0.80 | % | |
| Water absorption rate | Saturation, 23°C | ISO 62 | 0.12 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 0.090 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | -- 2 | ASTM D638 | 2180 | Mpa |
| -- | ISO 527-2/1 | 2300 | Mpa | |
| Tensile strength | Yield 3 | ASTM D638 | 57.0 | Mpa |
| Yield | ISO 527-2/50 | 56.0 | Mpa | |
| Break 3 | ASTM D638 | 59.0 | Mpa | |
| Break | ISO 527-2/50 | 55.0 | Mpa | |
| elongation | Yield 3 | ASTM D638 | 5.6 | % |
| Yield | ISO 527-2/50 | 5.4 | % | |
| Break 3 | ASTM D638 | 120 | % | |
| Break | ISO 527-2/50 | 110 | % | |
| Bending modulus | 50.0 mm Span 4 | ASTM D790 | 2180 | Mpa |
| -- 5 | ISO 178 | 2120 | Mpa | |
| Bending stress | -- 5, 6 | ISO 178 | 88.0 | Mpa |
| Yield, 50.0 mm Span 4 | ASTM D790 | 92.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Thermal deformation temperature under load | 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 120 | °C |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 9 | ISO 75-2/Af | 116 | °C | |
| Vicat softening temperature | -- | ASTM D152510, ISO 306/B5010 | 138 | °C |
| -- | ISO 306/B120 | 139 | °C | |
| Ball Pressure Test | 123 to 127°C | IEC 60695-10-2 | 通过 | |
| Linear coefficient of thermal expansion | Flow : -40 to 95°C | ASTM E831 | 6.7E-5 | cm/cm/°C |
| Flow : 23 to 80°C | ISO 11359-2 | 6.7E-5 | cm/cm/°C | |
| Across Flow : -40 to 95°C | ASTM E831 | 8.0E-5 | cm/cm/°C | |
| Across Flow : 23 to 80°C | ISO 11359-2 | 8.0E-5 | cm/cm/°C | |
| RTI Elec | UL 746 | 130 | °C | |
| RTI | UL 746 | 130 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | ASTM D257 | > 1.0E+15 | ohms | |
| Volume resistivity | ASTM D257 | > 1.0E+15 | ohms·cm |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 120 | °C | ||
| drying time | 3.0 到 4.0 | hr | ||
| Suggested maximum moisture content | 0.020 | % | ||
| Suggested injection volume | 40 到 60 | % | ||
| Temperature at the rear of the barrel | 270 到 295 | °C | ||
| Temperature in the middle of the barrel | 280 到 305 | °C | ||
| Temperature at the front of the material cylinder | 295 到 315 | °C | ||
| Spray nozzle temperature | 290 到 310 | °C | ||
| Processing (melt) temperature | 295 到 315 | °C | ||
| Mold temperature | 70 到 95 | °C | ||
| Back pressure | 0.300 到 0.700 | Mpa | ||
| Screw speed | 40 到 70 | rpm | ||
| Exhaust hole depth | 0.025 到 0.076 | mm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam gap 7 | -30°C | ISO 179/1eA | 60 | kJ/m² |
| 23°C | ISO 179/1eA | 70 | kJ/m² | |
| The impact strength of a simply supported beam without a notch is 7 | -30°C | ISO 179/1eU | 无断裂 | |
| 23°C | ISO 179/1eU | 无断裂 | ||
| Unscented Izod Impact Strength 8 | -30°C | ISO 180/1U | 无断裂 | |
| 23°C | ISO 180/1U | 无断裂 | ||
| Dart impact equipped with measuring instruments | -30°C, Total Energy | ASTM D3763 | 77.0 | J |
| 23°C, Total Energy | ASTM D3763 | 75.0 | J |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | L -Sale | ISO 2039-2 | 87 |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| transmissivity | 2540 µm | ASTM D1003 | 82.0 | % |
| Haze | 2540 µm | ASTM D1003 | 3.0 | % |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.8 mm | UL 94 | HB | |
| 3.0 mm | UL 94 | V-2 | ||
| Burning wire flammability index | 3.0 mm | IEC 60695-2-12 | 960 | °C |
| Hot filament ignition temperature | 0.8 mm | IEC 60695-2-13 | 850 | °C |
| 3.0 mm | IEC 60695-2-13 | 850 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.