Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Density | | ASTM D792/ISO 1183 | 1.38 | |
| Melt Mass-Flow Rate | | ASTM D1238/ISO 1133 | 35 cm3/10min(300℃/1.2kg ) | g/10min |
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | TD:2.00mm | 内部方法 | 0.50to0.60 | % |
| Modeling Shrinkage | MD:2.00mm | 内部方法 | 0.50to0.60 | % |
| Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 35.0 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Flexural Stress | | ISO178 | 80.0 | Mpa |
| Flexural Modulus | | ISO 178 | 2200 | Mpa |
| Nominal Tensile Strain at Break | | ISO527-2 | 70 | % |
| Tensile Stress | Yield | ISO527-2 | 50.0 | Mpa |
| Notched Impact Strength | | ISO 176 | 30 | k/Jm2 |
| Tensile Modulus | | ISO 527-1 | 2100 | Mpa |
| Tensile Stress(Yield) | | ISO 527-1 | 50 | Mpa |
| Tensile Elongation?(Break) | | ASTM D638/ISO 527 | tB 70 | % |
| Tensile Strength | | ASTM D638/ISO 527 | 50 | kg/cm²(MPa)[Lb/in²] |
| Tensile Elongation | Break | ISO 527-1 | 70 | % |
| Flexural Modulus | | ASTM D790/ISO 178 | 2.2(GPa) | kg/cm²(MPa)[Lb/in²] |
| Flexural Modulus | | ISO178 | 2200 | Mpa |
| Flexural Strength | | ASTM D790/ISO 178 | 80 | kg/cm²(MPa)[Lb/in²] |
| Flexural Strength | | ISO 178 | 80 | Mpa |
| Izod notch impact strength | | ASTM D256/ISO 179 | 30 | kg·cm/cm(J/M)ft·lb/in |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| RTIElec | | UL746 | 80.0 | °C |
| Evolution Calendar intelligent importer | | UL746 | 80.0 | °C |
| RTIStr | | UL746 | 80.0 | °C |
| Linear thermal expansion coefficient | MD | ISO11359-2 | 6.5E-05 | cm/cm/°C |
| Burning Rate | | UL94 | V0/1.0mm | |
| Deflection Temperature Under Load? | 1.8MPa | ISO 75-1-2 | 125 | °C |
| Deflection Temperature Under Load? | 0.46MPa | ISO 75-1-2 | 136 | °C |
| Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 136 | °C |
| Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 125 | °C |
| Flame retardancy | 1.0mm | UL94 | V-0 | |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Transmittance | 1000µm | ISO13468-1 | 0.1 | % |
| The Yellow Index | | | 9.0 | YI |
| Index of Refraction | | | 97.5 | |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Flame Rating | 1.0mm,NC | UL94 | V-0 | |
| Supplementary information | Test Condition | Test Method | Test Result | Unit |
|---|
| ISO Shortname | | | >PC-MD20< | |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|
| MVR | | ISO 1133 | 32 | cm3/10min |
| Index of Refraction | D65 type,10 | | 97.5 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.