PC LEXAN™ EXL1414 BK1A068 SABIC INNOVATIVE US

182

Unit Price:
$3333 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
35MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Processability Moderate liquidity Ductility copolymer Good demolding performanc
Application Areas:Electrical field Electronic field currency
Color:--
Grade:Injection grade

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	Across Flow : 3.20 mm	内部方法	0.40 到 0.80	%
Shrinkage rate	Shrinkage rate	Flow : 3.20 mm	内部方法	0.40 到 0.80	%
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.15	%
Water absorption rate	Water absorption rate	Saturation, 23°C	ISO 62	0.35	%
Melt flow rate	300°C/1.2 kg	ASTM D1238	10	g/10 min
Molten Volume Flow Rate (MVR)	300°C/1.2 kg	ISO 1133	9.00	cm3/10min

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile strength	Break	ISO 527-2/50	60.0	Mpa
	Tensile strength	Break 3	ASTM D638	50.0	Mpa
		Tensile strength	Yield	ISO 527-2/50	57.0	Mpa
		Tensile strength	Tensile strength	Yield 3	ASTM D638	55.0	Mpa
Tensile modulus	--	ISO 527-2/1	2150	Mpa
Tensile modulus	Tensile modulus	-- 2	ASTM D638	2020	Mpa
elongation	Break	ISO 527-2/50	120	%
	elongation	Break 3	ASTM D638	98	%
		elongation	Yield	ISO 527-2/50	6.0	%
		elongation	elongation	Yield 3	ASTM D638	6.0	%
Bending modulus	-- 5	ISO 178	2250	Mpa
Bending modulus	Bending modulus	50.0 mm Span 4	ASTM D790	2230	Mpa
Bending stress	Yield, 50.0 mm Span 4	ASTM D790	92.0	Mpa
Bending stress	Bending stress	-- 5, 6	ISO 178	85.0	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	7.0E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Flow : 23 to 80°C	ISO 11359-2	7.2E-5	cm/cm/°C
		Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	7.5E-5	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : 23 to 80°C	ISO 11359-2	7.2E-5	cm/cm/°C
Thermal deformation temperature under load	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	139	°C
	Thermal deformation temperature under load	0.45 MPa, Unannealed, 4.00 mm, 100 mm Span 9	ISO 75-2/Be	140	°C
		Thermal deformation temperature under load	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	124	°C
		Thermal deformation temperature under load	Thermal deformation temperature under load	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span 9	ISO 75-2/Ae	128	°C
Ball Pressure Test	123 to 127°C	IEC 60695-10-2	通过
Vicat softening temperature	--	ASTM D152510, ISO 306/B5010	145	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	146	°C
RTI		UL 746	125	°C
RTI Imp		UL 746	120	°C
RTI Elec		UL 746	130	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dissipation factor	100 Hz	ASTM D150	1.2E-3
Dissipation factor	Dissipation factor	1 MHz	ASTM D150	9.3E-3
Surface resistivity		ASTM D257	> 1.0E+15	ohms
Dielectric constant	100 Hz	ASTM D150	2.68
Dielectric constant	Dielectric constant	1 MHz	ASTM D150	2.64
Volume resistivity		ASTM D257	> 1.0E+15	ohms·cm
Dielectric strength	0.800 mm, in Oil	ASTM D149	16	KV/mm

injection	Test Result	Unit
drying time	3.0 到 4.0	hr
Suggested injection volume	40 到 60	%
Temperature at the rear of the barrel	215 到 295	°C
Temperature in the middle of the barrel	280 到 305	°C
Temperature at the front of the material cylinder	295 到 315	°C
Spray nozzle temperature	290 到 310	°C
Back pressure	0.300 到 0.700	Mpa
Screw speed	40 到 70	rpm
Exhaust hole depth	0.025 到 0.076	mm
drying temperature	120	°C
Suggested maximum moisture content	0.020	%
Processing (melt) temperature	295 到 315	°C
Mold temperature	70 到 95	°C

Impact performance	Test Condition	Test Method	Test Result	Unit
Dart impact equipped with measuring instruments	23°C, Total Energy	ASTM D3763	70.0	J
Impact strength of simply supported beam gap 7	23°C	ISO 179/1eA	70	kJ/m²
Impact strength of simply supported beam gap 7	Impact strength of simply supported beam gap 7	-30°C	ISO 179/1eA	65	kJ/m²
The impact strength of a simply supported beam without a notch is 7	-30°C	ISO 179/1eU	无断裂
	The impact strength of a simply supported beam without a notch is 7	23°C	ISO 179/1eU	无断裂
Unscented Izod Impact Strength 8	-30°C	ISO 180/1U	无断裂
Unscented Izod Impact Strength 8	Unscented Izod Impact Strength 8	23°C	ISO 180/1U	无断裂

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	R-Scale	ASTM D785	121
Rockwell hardness	Rockwell hardness	L -Sale	ASTM D785	89

flammability	Test Condition	Test Method	Test Result	Unit
Burning wire flammability index	0.8 mm	IEC 60695-2-12	850	°C
Burning wire flammability index	Burning wire flammability index	1.0 mm	IEC 60695-2-12	960	°C
Hot filament ignition temperature	1.0 mm	IEC 60695-2-13	875	°C
Hot filament ignition temperature	Hot filament ignition temperature	3.0 mm	IEC 60695-2-13	875	°C
UL flame retardant rating	0.40 mm	UL 94	HB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.