PC LEXAN™ EXL1414T SABIC INNOVATIVE NANSHA

135

Unit Price:
$4674 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
151.8MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Low temperature resistanc transparent Processability Moderate liquidity Ductility copolymer
Application Areas:Electrical field Electronic field Household appliances Household appliances Fitness equipment
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	MD:3.20mm	内部方法	0.40到0.80	%
Modeling Shrinkage	Modeling Shrinkage	TD:3.20mm	内部方法	0.40到0.80	%
Moisture Absorption	Saturation,23°C	ISO62	0.12	%
Moisture Absorption	Moisture Absorption	Equilibrium,23°C,50%RH	ISO62	0.093	%
Melt Mass-Flow Rate	300°C/1.2kg	ASTMD1238	10	g/10min
Melt Volume flow Rate	300°C/1.2kg	ISO1133	9.50	cm3/10min
Density / Specific Gravity		ASTMD792,ISO1183	1.19	g/cm³

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Stress	--6,7	ISO178	88.6	Mpa
Flexural Stress	Flexural Stress	Yield,50.0mmSpan5	ASTMD790	92.0	Mpa
Tensile Strength	Yield4	ASTMD638	57.6	Mpa
	Tensile Strength	Yield	ISO527-2/50	56.8	Mpa
		Tensile Strength	Break4	ASTMD638	59.1	Mpa
		Tensile Strength	Tensile Strength	Break	ISO527-2/50	55.3	Mpa
Tensile Modulus	--3	ASTMD638	2190	Mpa
Tensile Modulus	Tensile Modulus	--	ISO527-2/1	2310	Mpa
Tensile Elongation	Yield4	ASTMD638	5.6	%
	Tensile Elongation	Yield	ISO527-2/50	5.4	%
		Tensile Elongation	Break4	ASTMD638	120	%
		Tensile Elongation	Tensile Elongation	Break	ISO527-2/50	110	%
Flexural Modulus	50.0mmSpan5	ASTMD790	2180	Mpa
Flexural Modulus	Flexural Modulus	--6	ISO178	2120	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	1.8MPa,Unannealed,3.20mm	ASTMD648	121	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,Unannealed,64.0mmSpan10	ISO75-2/Af	116	°C
RTIElec		UL746	130	°C
Linear thermal expansion coefficient	MD:23to80°C	ISO11359-2	6.7E-05	cm/cm/°C
	Linear thermal expansion coefficient	TD:-40to95°C	ASTME831	8E-05	cm/cm/°C
		Linear thermal expansion coefficient	TD:23to80°C	ISO11359-2	8E-05	cm/cm/°C
		Linear thermal expansion coefficient	Linear thermal expansion coefficient	MD:-40to95°C	ASTME831	6.7E-05	cm/cm/°C
RTI		UL746	130	°C
Ball PressureTest	125°C	IEC60695-10-2	通过
Vicat Softening Temperature	--	ASTMD152511,ISO306/B12011	139	°C
Vicat Softening Temperature	Vicat Softening Temperature	--	ISO306/B50	138	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface Resistivity		ASTMD257	>1.0E+15	ohms
Volume Resistivity		ASTMD257	>1.0E+15	ohms·cm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Instrumented Dart Impact	-30°C,TotalEnergy	ASTMD3763	77.4	J
Instrumented Dart Impact	Instrumented Dart Impact	23°C,TotalEnergy	ASTMD3763	75.5	J
Charpy Notched Impact Strength	-30°C	ISO179/1eA	60	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO179/1eA	70	kJ/m²
Charpy Unnotched Impact Strength	-30°C	ISO179/1eU	无断裂
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO179/1eU	无断裂
Unnotched Izod Impact Strength	-30°C	ISO180/1U	无断裂
Unnotched Izod Impact Strength	Unnotched Izod Impact Strength	23°C	ISO180/1U	无断裂
Notched Izod Impact Strength	-30°C	ASTMD256	710	J/m
	Notched Izod Impact Strength	23°C	ASTMD256	820	J/m
		Notched Izod Impact Strength	-30°C9	ISO180/1A	55	kJ/m²
		Notched Izod Impact Strength	Notched Izod Impact Strength	23°C9	ISO180/1A	65	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	L-Sale	ISO2039-2	87

optical performance	Test Condition	Test Method	Test Result	Unit
Haze	2540µm	ASTMD1003	3.0	%
Transmittance	2540µm	ASTMD1003	82.0	%

Flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.8mm	UL94	HB
UL flame retardant rating	UL flame retardant rating	3.0mm	UL94	V-2
Glow Wire Flammability Index	3.0mm	IEC60695-2-12	960	°C
Glow Wire Ignition Temperature	0.8mm	IEC60695-2-13	850	°C
Glow Wire Ignition Temperature	Glow Wire Ignition Temperature	3.0mm	IEC60695-2-13	850	°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.