PC LEXAN™ EXL1414-WH9A320 SABIC INNOVATIVE SHANGHAI

Unit Price:
$5281 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Processability Moderate liquidity Ductility copolymer Good demolding performanc
Application Areas:Electrical applications Home appliance components Fitness equipment
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	Flow : 3.20 mm	内部方法	0.40 到 0.80	%
Modeling Shrinkage	Modeling Shrinkage	Across Flow : 3.20 mm	内部方法	0.40 到 0.80	%
Moisture Absorption	Saturation, 23°C	ISO 62	0.35	%
Moisture Absorption	Moisture Absorption	Equilibrium, 23°C, 50% RH	ISO 62	0.15	%
Melt Mass-Flow Rate	300°C/1.2 kg	ASTM D1238	10	g/10 min
Melt Volume flow Rate	300°C/1.2 kg	ISO 1133	9.00	cm3/10min
Density / Specific Gravity	--	ASTM D792	1.18	g/cm³
Density / Specific Gravity	Density / Specific Gravity	--	ISO 1183	1.19	g/cm³

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Stress	-- 5, 6	ISO 178	85.0	Mpa
Flexural Stress	Flexural Stress	Yield, 50.0 mm Span 4	ASTM D790	92.0	Mpa
Tensile Strength	Yield 3	ASTM D638	55.0	Mpa
	Tensile Strength	Yield	ISO 527-2/50	57.0	Mpa
		Tensile Strength	Break 3	ASTM D638	50.0	Mpa
		Tensile Strength	Tensile Strength	Break	ISO 527-2/50	60.0	Mpa
Tensile Modulus	-- 2	ASTM D638	2020	Mpa
Tensile Modulus	Tensile Modulus	--	ISO 527-2/1	2150	Mpa
Tensile Elongation	Yield 3	ASTM D638	6.0	%
	Tensile Elongation	Yield	ISO 527-2/50	6.0	%
		Tensile Elongation	Break 3	ASTM D638	98	%
		Tensile Elongation	Tensile Elongation	Break	ISO 527-2/50	120	%
Flexural Modulus	50.0 mm Span 4	ASTM D790	2230	Mpa
Flexural Modulus	Flexural Modulus	-- 5	ISO 178	2250	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Vicat Softening Temperature	--	ASTM D152510, ISO 306/B5010	145	°C
Vicat Softening Temperature	Vicat Softening Temperature	--	ISO 306/B120	146	°C
RTI		UL 746	125	°C
RTI Imp		UL 746	120	°C
RTI Elec		UL 746	130	°C
Linear thermal expansion coefficient	Flow : -40 to 40°C	ASTM E831	7.0E-5	cm/cm/°C
	Linear thermal expansion coefficient	Flow : 23 to 80°C	ISO 11359-2	7.2E-5	cm/cm/°C
		Linear thermal expansion coefficient	Across Flow : -40 to 40°C	ASTM E831	7.5E-5	cm/cm/°C
		Linear thermal expansion coefficient	Linear thermal expansion coefficient	Across Flow : 23 to 80°C	ISO 11359-2	7.2E-5	cm/cm/°C
Deflection Temperature Under Load?	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	139	°C
	Deflection Temperature Under Load?	0.45 MPa, Unannealed, 4.00 mm, 100 mm Span 9	ISO 75-2/Be	140	°C
		Deflection Temperature Under Load?	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	124	°C
		Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span 9	ISO 75-2/Ae	128	°C
Ball PressureTest	123 to 127°C	IEC 60695-10-2	通过

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric Strength	0.800 mm, in Oil	ASTM D149	16	KV/mm
Dissipation Factor?	100 Hz	ASTM D150	1.2E-3
Dissipation Factor?	Dissipation Factor?	1 MHz	ASTM D150	9.3E-3
Surface Resistivity		ASTM D257	> 1.0E+15	ohms
Dielectric Constant	100 Hz	ASTM D150	2.68
Dielectric Constant	Dielectric Constant	1 MHz	ASTM D150	2.64
Volume Resistivity		ASTM D257	> 1.0E+15	ohms·cm

Injection	Test Result	Unit
Drying Temperature	120	°C
Suggested Max Moisture	0.020	%
Processing (Melt) Temp	295 到 315	°C
Mold Temperature	70 到 95	°C
Drying Time	3.0 到 4.0	hr
Suggested Shot Size	40 到 60	%
Rear Temperature	270 到 295	°C
Middle Temperature	280 到 305	°C
Front Temperature	295 到 315	°C
Nozzle Temperature	290 到 310	°C
Back Pressure	0.300 到 0.700	Mpa
Screw Speed	40 到 70	rpm
Vent Depth	0.025 到 0.076	mm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Instrumented Dart Impact	23°C, Total Energy	ASTM D3763	70.0	J
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	65	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	70	kJ/m²
Charpy Unnotched Impact Strength	-30°C	ISO 179/1eU	无断裂
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO 179/1eU	无断裂
Unnotched Izod Impact Strength	-30°C	ISO 180/1U	无断裂
Unnotched Izod Impact Strength	Unnotched Izod Impact Strength	23°C	ISO 180/1U	无断裂
Notched Izod Impact Strength	-30°C	ASTM D256	770	J/m
	Notched Izod Impact Strength	23°C	ASTM D256	870	J/m
		Notched Izod Impact Strength	-30°C 8	ISO 180/1A	60	kJ/m²
		Notched Izod Impact Strength	Notched Izod Impact Strength	23°C 8	ISO 180/1A	70	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	L -Sale	ASTM D785	89
Rockwell Hardness	Rockwell Hardness	R-Scale	ASTM D785	121

Flammability	Test Condition	Test Method	Test Result	Unit
Glow Wire Flammability Index	0.8 mm	IEC 60695-2-12	850	°C
Glow Wire Flammability Index	Glow Wire Flammability Index	1.0 mm	IEC 60695-2-12	960	°C
Glow Wire Ignition Temperature	1.0 mm	IEC 60695-2-13	875	°C
Glow Wire Ignition Temperature	Glow Wire Ignition Temperature	3.0 mm	IEC 60695-2-13	875	°C
Flame Rating	0.40 mm	UL 94	HB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.