Material Description

Technical Data Sheet

Material Description

Material Properties:Low temperature resistanc Flame retardant
Application Areas:Electronic display Lighting applications
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Moisture Absorption	24 hr	ASTM D570	0.15	%
	Moisture Absorption	Equilibrium, 23°C	ASTM D570	0.35	%
	Moisture Absorption	Moisture Absorption	Equilibrium, 100°C	ASTM D570	0.58	%
Specific Volume		ASTM D792	0.830	cm³/g
Outdoor Suitability		UL 746C	f2
Melt Mass-Flow Rate	300°C/1.2 kg	ASTM D1238	18	g/10 min
Modeling Shrinkage - Flow	3.20 mm	内部方法	0.50 到 0.70	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Taber Abrasion Resistance	1000 Cycles, 1000 g, CS-17 Wheel	ASTM D1044	10.0	mg
Tensile Strength	Yield	ASTM D638	62.0	Mpa
Tensile Strength	Tensile Strength	Break	ASTM D638	68.0	Mpa
Tensile Elongation	Yield	ASTM D638	7.0	%
Tensile Elongation	Tensile Elongation	Break	ASTM D638	130	%
Flexural Modulus	50.0 mm Span	ASTM D790	2340	Mpa
Flexural Strength	Yield, 50.0 mm Span	ASTM D790	96.0	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
RTI		UL 746	130	°C
RTI Imp		UL 746	130	°C
RTI Elec		UL 746	130	°C
Deflection Temperature Under Load?	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	137	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	129	°C
Vicat Softening Temperature		ASTM D15255	154	°C
Specific Heat		ASTM C351	1250	J/kg/°C
Thermal Conductivity		ASTM C177	0.25	W/m/K
Coefficient of Linear Thermal Expansion (Flow)	-40 to 95°C	ASTM E831	6.8E-5	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Comparative Tracking Index		UL 746	PLC 2
Hot-wire Ignition		UL 746	PLC 2
High Amp Arc Ignition		UL 746	PLC 1
High Voltage Arc Tracking Rate		UL 746	PLC 2
Dielectric Constant	60 Hz	ASTM D150	3.17
	Dielectric Constant	50 kHz	ASTM D150	3.17
	Dielectric Constant	Dielectric Constant	1 MHz	ASTM D150	2.96
Volume Resistivity		ASTM D257	> 1.0E+17	ohms·cm
Dissipation Factor?	50 Hz	ASTM D150	9.0E-4
	Dissipation Factor?	60 Hz	ASTM D150	9.0E-4
	Dissipation Factor?	Dissipation Factor?	1 MHz	ASTM D150	0.010
Dielectric Strength	3.20 mm, in Air	ASTM D149	15	KV/mm

Injection	Test Result	Unit
Drying Time	3.0 到 4.0	hr
Suggested Shot Size	40 到 60	%
Rear Temperature	260 到 280	°C
Middle Temperature	270 到 295	°C
Front Temperature	280 到 305	°C
Nozzle Temperature	275 到 300	°C
Back Pressure	0.300 到 0.700	Mpa
Screw Speed	40 到 70	rpm
Vent Depth	0.025 到 0.076	mm
Drying Temperature	120	°C
Suggested Max Moisture	0.020	%
Processing (Melt) Temp	280 到 305	°C
Mold Temperature	70 到 95	°C

Impact Properties	Test Condition	Test Method	Test Result	Unit
Gardner Impact	23°C	ASTM D3029	169	J
Instrumented Dart Impact	23°C, Energy at Peak	ASTM D3763	62.0	J
Tensile Impact Strength		ASTM D1822	546	kJ/m²
Unnotched Izod Impact Strength	23°C	ASTM D4812	3200	J/m

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	M-Scale	ASTM D785	70
Rockwell Hardness	Rockwell Hardness	R-Scale	ASTM D785	118

optical performance	Test Condition	Test Method	Test Result	Unit
Refractive index of light		ASTM D542	1.586
Haze	2540 µm	ASTM D1003	1.0	%
Transmittance	2540 µm	ASTM D1003	88.0	%

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating	1.1 mm	UL 94	V-2
Flame Rating	Flame Rating	6.0 mm	UL 94	V-0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.