PC TARFLON™ AZ1900T IDEMITSU JAPAN

153

Unit Price:
$6573 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Flame retardant
Application Areas:Home appliance components Automotive Applications
Color:--
Grade:High liquidity level

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Density		ASTM D792/ISO 1183	1.20
Modeling Shrinkage		ASTM D955	0.5~0.7	%

Physical Properties	Test Condition	Test Method	Test Result	Unit
Moisture Absorption	Equilibrium, 23℃, 50% RH	ISO 62	0.23	%
Moisture Absorption	Moisture Absorption	Equilibrium, 23°C, 50% RH	ISO 62	0.23	%
Modeling Shrinkage	TD	Internal Method	0.5-0.7	%
	Modeling Shrinkage	MD: 2.00 mm	Internal Method	0.5-0.7	%
		Modeling Shrinkage	Across Flow : 2.00 mm	内部方法	0.50 到 0.70	%
			Modeling Shrinkage	流量 : 2.00 mm	内部方法	0.50 到 0.70	%
				Modeling Shrinkage	TD:2.00mm	内部方法	0.50to0.70	%
				Modeling Shrinkage	Modeling Shrinkage	MD:2.00mm	内部方法	0.50to0.70	%
Melt Volume flow Rate	300°C/1.2kg	ISO1133	5.00	cm3/10min
Melt Volume flow Rate	MVR	ISO 1133	5	cm3/10min
Spiral Flow		内部方法	48.0	CM
Moisture Absorption	Equilibrium,23°C,50%RH	ISO62	0.23	%
Melt Volume flow Rate	300°C/1.2 kg	ISO 1133	18.0	cm3/10min
Spiral Flow?3,?4		内部方法	29.0	CM

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Charpy Notched Impact Strength		ISO 179	65	kJ/m²
Tensile Elongation (Break)		ISO 527-2	70	%
Nominal Tensile Strain at Break		ISO 527-2	95	%
Nominal Tensile Strain at Break	Nominal Tensile Strain at Break		ISO527-2	70	%
Tensile Elongation?(Break)		ASTM D638/ISO 527	92	%
Tensile Modulus		ASTM D638/ISO 527	2300	kg/cm²(MPa)[Lb/in²]
Tensile Strength		ASTM D638/ISO 527	68	kg/cm²(MPa)[Lb/in²]
Tensile Elongation		ASTM D638/ISO 527	64	%
Flexural Modulus		ASTM D790/ISO 178	2400	kg/cm²(MPa)[Lb/in²]
	Flexural Modulus		ISO 178	2300	Mpa
	Flexural Modulus	Flexural Modulus		ISO178	2300	Mpa
Flexural Strength		ISO 178	90	Mpa
Tensile Stress	Yield	ISO527-2	65.0	Mpa
	Tensile Stress	Yield	ISO 527-2	65.0	Mpa
	Tensile Stress	Tensile Stress	Yield	ISO 527-2	65	Mpa
Flexural Stress		ISO 178	90.0	Mpa
Flexural Stress	Flexural Stress		ISO178	90.0	Mpa
Tensile Elongation?(Break)		ASTM D638/ISO 527	92	%
Izod notch impact strength		ASTM D256/ISO 179	80	kg·cm/cm(J/M)ft·lb/in

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Coefficient of Linear Thermal Expansion (Flow)		ASTM D696	0.000065	cm/cm/℃
Coefficient of Linear Thermal Expansion (Flow)		ISO 11359-2	6.5E-5	cm/cm/°C
RTI		UL 746	80.0	°C
RTI Imp		UL 746	80.0	°C
RTI Elec		UL 746	80.0	°C
RTIElec		UL746	80.0	°C
Evolution Calendar intelligent importer		UL746	80.0	°C
RTIStr		UL746	80.0	°C
Linear thermal expansion coefficient	MD	ISO11359-2	6.5E-05	cm/cm/°C
Burning Rate		UL94	V-0/1.5mm
Deflection Temperature Under Load?		ASTM D648/ISO 75	131	℃（℉）
	Deflection Temperature Under Load?	1.8 MPa, Unannealed	ISO 75-2/A	125	°C
		Deflection Temperature Under Load?	1.8 MPa, Unannealed	ISO 75-2/A	125	°C
			Deflection Temperature Under Load?	0.45MPa,Unannealed	ISO75-2/B	140	°C
			Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,Unannealed	ISO75-2/A	125	°C
Flame Rating	1.50 mm	UL 94	V-0
Flame Rating	Flame Rating	4.00 mm	UL 94	5VA

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric Constant	1 MHz	IEC 60250	2.85
	Dielectric Constant	1MHz	IEC60250	2.85
	Dielectric Constant	Dielectric Constant	1 MHz	IEC 60250	2.85
Dielectric Strength		IEC60243-1	30	KV/mm
Dielectric Strength	Dielectric Strength		IEC 60243-1	30	KV/mm
Comparative Tracking Index		UL 746	PLC 2

Injection	Test Result	Unit
Drying Time	5.0 到 8.0	hr
Rear Temperature	260 到 300	°C
Middle Temperature	260 到 300	°C
Front Temperature	260 到 300	°C
Drying Temperature	120	°C
Mold Temperature	80 到 120	°C

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	M-Sale	ISO2039-2	50
	Rockwell Hardness	R-Sale	ISO2039-2	120
		Rockwell Hardness	M -Sale	ISO 2039-2	50
		Rockwell Hardness	Rockwell Hardness	R -Sale	ISO 2039-2	120

optical performance	Test Condition	Test Method	Test Result	Unit
Transmittance		ISO13468-1	85.0to89.0	%

Flammability	Test Condition	Test Method	Test Result
ISO Shortname			>PC<
UL flame retardant rating	1.5mm	UL94	V-0
Flame Rating	1.5 mm	UL 94	V-0

Supplementary information	Test Condition	Test Method	Test Result	Unit
ISO Shortname			>PC<

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.