PC TARFLON™ IRY2200 IDEMITSU JAPAN
152
- Unit Price:
- $3250 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 25MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:transparent Flame retardant High temperature resistan Low viscosity
- Application Areas:currency
- Color:--
- Grade:Weather resistant grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density | ASTM D792/ISO 1183 | 1.2 | ||
| Modeling Shrinkage | ASTM D955 | 0.5-0.7 | % | |
| Moisture Absorption 23℃/24H | ASTM D570/ISO 62 | 0.23 | % | |
| Melt Mass-Flow Rate | ASTM D1238/ISO 1133 | 12 cm3/10min(300℃/1.2kg ) | g/10min |
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Light Transmittance | 85～89 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Elongation?(Break) | ASTM D638/ISO 527 | tB 90 | % | |
| Tensile Strength | ASTM D638/ISO 527 | Y 65 | kg/cm²(MPa)[Lb/in²] | |
| Rockwell Hardness | ASTM D785 | R120,M50 | ||
| Flexural Modulus | ASTM D790/ISO 178 | 2.3(GPa) | kg/cm²(MPa)[Lb/in²] | |
| Flexural Strength | ASTM D790/ISO 178 | 90 | kg/cm²(MPa)[Lb/in²] | |
| Flexural Modulus | 2350 | Mpa | ||
| Tensile Strength | 93 | Mpa | ||
| Rockwell Hardness | R120（M75） | |||
| Tensile Strength (Break) | 68 | Mpa | ||
| Tensile Elongation (Break) | 115 | % | ||
| Tensile Elongation (Yield) | 64 | Mpa | ||
| 滑动摩擦 | 12 | |||
| 伸张弹性模量 | 2300 | Mpa | ||
| Izod Impact Strength | 3.2mm | 90 | KJ/m | |
| 4mm | 70 | KJ/m | ||
| Izod notch impact strength | ASTM D256/ISO 179 | 80 | kg·cm/cm(J/M)ft·lb/in |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flammability | 3mm | V-0 | ||
| Burning Rate | UL94 | V0/3.0mm | ||
| Vicat Softening Temperature | 148 | °C | ||
| Linear expansion coefficient | ASTM D696/ISO 11359 | 6.5 | mm/mm.℃ | |
| Deflection Temperature Under Load | 148 | °C | ||
| Coefficient of Linear Thermal Expansion | 6.5 |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Insulation Resistance | 30 | KV/mm | ||
| Dissipation Factor | 1MHz | 9.2×10 | ||
| 60Hz | 6.6×10 | |||
| Volume Resistivity | ＜10 | Ω.m | ||
| Relative Permittivity | 1MHz | 2.85 | ||
| 60Hz | 2.91 | |||
| Dielectric Constant | ASTM D150/IEC 60250 | 2.85 | ||
| Arc Resistance | 110 | sec |
| Processing | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | 0.5～0.7% | % |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Moisture Absorption | 0.23 | % | ||
| Melt index | 12 | g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.