Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density | | ASTM D792/ISO 1183 | 1470 | |
Modeling Shrinkage | | ASTM D955 | 0.02-0.2 | % |
Moisture Absorption 23℃/24H | | ASTM D570/ISO 62 | 0.12 | % |
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | TD:4.00mm | 内部方法 | 0.30to0.50 | % |
Modeling Shrinkage | MD:4.00mm | 内部方法 | 0.020to0.20 | % |
Moisture Absorption | 23°C,24hr | ISO62 | 0.12 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | Break | ISO527-2/5 | 105 | Mpa |
Tensile Strain | Break | ISO527-2/5 | 2.0 | % |
Tensile Modulus | | ASTM D638/ISO 527 | 8500 | kg/cm²(MPa)[Lb/in²] |
Tensile Modulus | | ISO527-2/1 | 8500 | Mpa |
Flexural Modulus | | ASTM D790/ISO 178 | 7600 | kg/cm²(MPa)[Lb/in²] |
Flexural Strength | | ASTM D790/ISO 178 | 155 | kg/cm²(MPa)[Lb/in²] |
Flexural Modulus | | ISO178 | 7600 | Mpa |
Flexural Stress | | ISO178 | 155 | Mpa |
Izod notch impact strength | | ASTM D256/ISO 179 | 30 | kg·cm/cm(J/M)ft·lb/in |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Vicat Softening Temperature | | ISO306/B50 | 153 | °C |
Linear thermal expansion coefficient | MD | ISO11359-2 | 2E-05 | cm/cm/°C |
Linear thermal expansion coefficient | TD | ISO11359-2 | 6E-05 | cm/cm/°C |
RTIElec | 1.5mm | UL746 | 130 | °C |
Evolution Calendar intelligent importer | 1.5mm | UL746 | 120 | °C |
RTIStr | 1.5mm | UL746 | 130 | °C |
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 151 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 148 | °C |
Vicat Softening Temperature | | ASTM D1525/ISO R306 | 153 | ℃(℉) |
Linear expansion coefficient | | ASTM D696/ISO 11359 | 0.2 | mm/mm.℃ |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Surface Resistivity | | IEC60093 | >1.0E+15 | ohms |
Volume Resistivity | | IEC60093 | >1.0E+15 | ohms·cm |
Dissipation Factor? | 100Hz | IEC60250 | 1E-03 | |
Dissipation Factor? | 1MHz | IEC60250 | 9E-03 | |
Relative Permittivity | 100Hz | IEC60250 | 3.50 | |
Relative Permittivity | 1MHz | IEC60250 | 3.50 | |
Comparative Tracking Index | | IEC60112 | 175 | V |
Dielectric Strength | | IEC60243-1 | 35 | KV/mm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | | ISO179 | 30 | kJ/m² |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 0.40mm | UL94 | V-2 | |
UL flame retardant rating | 0.75mm | UL94 | V-0 | |
UL flame retardant rating | 2.5mm | UL94 | 5VA | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.