Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | Across Flow : 4.00 mm | 内部方法 | 0.50 到 0.70 | % |
Modeling Shrinkage | 流量 : 4.00 mm | 内部方法 | 0.50 到 0.70 | % |
Moisture Absorption | 24 hr, 23°C | ISO 62 | 0.20 | % |
Melt Volume flow Rate | 300°C/1.2 kg | ISO 1133 | 8.00 | cm3/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Flexural Modulus | | ISO 178 | 2350 | Mpa |
Flexural Stress | | ISO 178 | 93.0 | Mpa |
Tensile Stress | Yield | ISO 527-2/50 | 61.0 | Mpa |
Tensile Strain | Yield | ISO 527-2/50 | 6.0 | % |
Tensile Modulus | | ISO 527-2/1 | 2400 | Mpa |
Nominal Tensile Strain at Break | | ISO 527-2/50 | > 50 | % |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Linear thermal expansion coefficient | Flow | ISO 11359-2 | 7.0E-5 | cm/cm/°C |
Linear thermal expansion coefficient | Across Flow | ISO 11359-2 | 7.0E-5 | cm/cm/°C |
Deflection Temperature Under Load? | 0.45 MPa, Unannealed | ISO 75-2/B | 142 | °C |
Deflection Temperature Under Load? | 1.8 MPa, Unannealed | ISO 75-2/A | 129 | °C |
Vicat Softening Temperature | | ISO 306/B50 | 149 | °C |
RTI | 0.75 mm | UL 746 | 125 | °C |
RTI Imp | 0.75 mm | UL 746 | 115 | °C |
RTI Elec | 0.75 mm | UL 746 | 125 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dielectric Strength | | IEC 60243-1 | 30 | KV/mm |
Surface Resistivity | | IEC 60093 | > 1.0E+15 | ohms |
Volume Resistivity | | IEC 60093 | > 1.0E+15 | ohms·cm |
Relative Permittivity | 100 Hz | IEC 60250 | 3.10 | |
Relative Permittivity | 1 MHz | IEC 60250 | 3.00 | |
Comparative Tracking Index | | IEC 60112 | 225 | V |
Dissipation Factor? | 100 Hz | IEC 60250 | 1.0E-3 | |
Dissipation Factor? | 1 MHz | IEC 60250 | 9.0E-3 | |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | | ISO 179 | 无断裂 | |
optical performance | Test Condition | Test Method | Test Result | Unit |
---|
Transmittance | 3000 µm | ASTM D1003 | 88.0 | % |
Refractive index of light | | ASTM D542 | 1.585 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Glow Wire Flammability Index | 1.5 mm | IEC 60695-2-12 | 825 | °C |
Glow Wire Flammability Index | 3.0 mm | IEC 60695-2-12 | 960 | °C |
Glow Wire Ignition Temperature | 1.5 mm | IEC 60695-2-13 | 850 | °C |
Glow Wire Ignition Temperature | 3.0 mm | IEC 60695-2-13 | 875 | °C |
Flame Rating | 0.40 mm | UL 94 | V-2 | |
Flame Rating | 1.5 mm | UL 94 | V-2 | |
Flame Rating | 3.0 mm | UL 94 | V-2 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.