Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density | | ASTM D792/ISO 1183 | 1.2 | |
Moisture Absorption 23℃/24H | | ASTM D570/ISO 62 | 0.15 | % |
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | Across Flow | | 0.7 | % |
Modeling Shrinkage | Flow | | 0.5 | % |
Moisture Absorption | 23℃,24h | ASTM D-570 | 0.15 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Strength | | ASTM D638/ISO 527 | 61.7 | kg/cm²(MPa)[Lb/in²] |
Tensile Strength | | ASTM D-638 | 61.7 | Mpa |
Rockwell Hardness | | ASTM D785 | R120 | |
Rockwell Hardness | | ASTM D-785 | R120 | R-Scale |
Flexural Modulus | | ASTM D-790 | 2.3 | GPa |
Flexural Modulus | | ASTM D790/ISO 178 | 2.3 | kg/cm²(MPa)[Lb/in²] |
Flexural Strength | | ASTM D790/ISO 178 | 88.2 | kg/cm²(MPa)[Lb/in²] |
Flexural strength | | ASTM D-790 | 88.2 | Mpa |
Tensile Elongation | | ASTM D-638 | 110 | % |
Heat Deflection Temperature | 18.6kgf/cm3 | ASTM D-648 | 135 | °C |
Heat Deflection Temperature | 4.6kgf/cm3 | ASTM D-648 | 145 | °C |
Notched Izod Impact Strength | 3.2mm | ASTM D-256 | 880 | J/m |
Izod notch impact strength | | ASTM D256/ISO 179 | 880 | kg·cm/cm(J/M)ft·lb/in |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Linear expansion coefficient | | ASTM D696/ISO 11359 | 5.6 | mm/mm.℃ |
Coefficient of Linear Thermal Expansion | | - | 5.6 | 10-5.k-1 |
Flammability | | UL94 | V-2 | - |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dielectric Constant | 106Hz | ASTM D-150 | 25.2 | Pf/m |
Dielectric Constant | | ASTM D150/IEC 60250 | 25.2 | |
Volume Resistivity | | ASTM D257/IEC 60093 | 4×1016 | Ω.cm |
Dielectric loss | | ASTM D150/IEC 60250 | 0.0092 | |
Arc Resistance | | ASTM D-149 | 16 | KV/mm |
Dissipation Factor?(Tangent) | 106Hz | ASTM D-150 | 0.0092 | - |
Volume Resistivity | | ASTM D-257 | 4×1016 | - |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.