Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.50到0.70 | % |
| Moisture Absorption | 24hr | ASTMD570 | 0.15 | % |
| Moisture Absorption | Equilibrium,23°C | ASTMD570 | 0.35 | % |
| Moisture Absorption | Equilibrium,100°C | ASTMD570 | 0.58 | % |
| Melt Mass-Flow Rate | 300°C/1.2kg | ASTMD1238 | 11 | g/10min |
| Specific Volume | | ASTMD792 | 0.835 | cm³/g |
| Outdoor Suitability | | UL746C | f2 | |
| Density / Specific Gravity | -- | ASTMD792 | 1.20 | g/cm³ |
| Density / Specific Gravity | -- | ASTMD792 | 1.19 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Strength | Break | ASTMD638 | 68.9 | Mpa |
| Tensile Strength | Yield | ASTMD638 | 62.1 | Mpa |
| Flexural Modulus | 50.0mmSpan | ASTMD790 | 2340 | Mpa |
| Flexural Strength | Yield,50.0mmSpan | ASTMD790 | 96.5 | Mpa |
| Tensile Elongation | Break | ASTMD638 | 130 | % |
| Tensile Elongation | Yield | ASTMD638 | 7.0 | % |
| Taber Abrasion Resistance | 1000Cycles,1000g,CS-17Wheel | ASTMD1044 | 10.0 | mg |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Linear thermal expansion coefficient | MD：-40to95°C | ASTME831 | 6.8E-05 | cm/cm/°C |
| Deflection Temperature Under Load? | 0.45MPa,Unannealed,6.40mm | ASTMD648 | 138 | °C |
| Deflection Temperature Under Load? | 1.8MPa,Unannealed,6.40mm | ASTMD648 | 132 | °C |
| RTIElec | | UL746 | 130 | °C |
| Evolution Calendar intelligent importer | | UL746 | 130 | °C |
| Vicat Softening Temperature | | ASTMD15256 | 154 | °C |
| Specific Heat | | ASTMC351 | 1260 | J/kg/°C |
| Thermal Conductivity | | ASTMC177 | 0.27 | W/m/K |
| RTI | | UL746 | 130 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Comparative Tracking Index | CTI | UL746 | PLC2 | |
| Hot-wire Ignition | HWI | UL746 | PLC2 | |
| High Amp Arc Ignition | HAI | UL746 | PLC1 | |
| High Voltage Arc Tracking Rate | HVTR | UL746 | PLC2 | |
| Dissipation Factor? | 50Hz | ASTMD150 | 9E-04 | |
| Dissipation Factor? | 60Hz | ASTMD150 | 9E-04 | |
| Dissipation Factor? | 1MHz | ASTMD150 | 0.010 | |
| Dielectric Constant | 1MHz | ASTMD150 | 2.96 | |
| Dielectric Constant | 50Hz | ASTMD150 | 3.17 | |
| Dielectric Constant | 60Hz | ASTMD150 | 3.17 | |
| Volume Resistivity | | ASTMD257 | >1.0E+17 | ohms·cm |
| Dielectric Strength | 3.20mm,inAir | ASTMD149 | 15 | KV/mm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Unnotched Izod Impact Strength | 23°C | ASTMD4812 | 3200 | J/m |
| Tensile Impact Strength | | ASTMD1822 | 578 | kJ/m² |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 63.8 | J |
| Gardner Impact | 23°C | ASTMD3029 | 169 | J |
| Notched Izod Impact Strength | 23°C | ASTMD256 | 800 | J/m |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | R-Scale | ASTMD785 | 118 | |
| Rockwell Hardness | M-Scale | ASTMD785 | 70 | |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Haze | 2540µm | ASTMD1003 | 1.0 | % |
| Refractive index of light | | ASTMD542 | 1.586 | |
| Transmittance | 2540µm | ASTMD1003 | 88.0 | % |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 0.71mm | UL94 | HB | |
| Radiant Panel Listing | UL | | YES | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.