Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | MD | ASTMD955 | 2.0 | % |
Modeling Shrinkage | TD | ISO294-4 | 2.2 | % |
Modeling Shrinkage | MD | ISO294-4 | 2.3 | % |
Moisture Absorption | 23°C,24hr | ISO62 | 0.53 | % |
Moisture Absorption | Equilibrium,23°C,60%RH | ASTMD570 | 0.22 | % |
Melt Mass-Flow Rate | 190°C/2.16kg | ASTMD1238 | 14 | g/10min |
Melt Mass-Flow Rate | 190°C/2.16kg | ISO1133 | 15 | g/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Strength | 23°C | ASTMD638 | 66.0 | Mpa |
Flexural Stress | 23°C | ISO178 | 95.0 | Mpa |
Tensile Stress | Yield,23°C | ISO527-2 | 67.0 | Mpa |
Tensile Strain | Break,23°C | ISO527-2 | 30 | % |
Tensile Elongation | Break,23°C | ASTMD638 | 55 | % |
Flexural Modulus | 23°C | ASTMD790 | 2900 | Mpa |
Flexural Modulus | 23°C | ISO178 | 2950 | Mpa |
Flexural Strength | 23°C | ASTMD790 | 98.0 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ASTMD648A | 158 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ASTMD648A | 110 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 100 | °C |
Vicat Softening Temperature | | ASTMD1525 | 162 | °C |
Linear thermal expansion coefficient | MD | ASTMD696 | 1.3E-05 | cm/cm/°C |
Melting temperature | | ISO11357-3 | 173 | °C |
Melting temperature | | ASTMD1525 | 173 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dielectric Strength | | ASTMD149 | 19 | KV/mm |
Dielectric Strength | | IEC60243-1 | 19 | KV/mm |
Surface Resistivity | | ASTMD257 | 1E+16 | ohms |
Surface Resistivity | | IEC60093 | 1E+16 | ohms |
Dielectric Constant | | ASTMD150 | 3.70 | |
Volume Resistivity | | ASTMD257 | 1E+14 | ohms·cm |
Volume Resistivity | | IEC60093 | 1E+14 | ohms·cm |
Dissipation Factor? | 1MHz | ASTMD150 | 6E-03 | |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | M-Scale | ASTMD785 | 82 | |
Rockwell Hardness | M-Scale | ISO2039-2 | 96 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 0.8mm | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.